Copper Coated Steel Strps Brass

China Copper Coated Steel Strps Brass, Find details about China Copper Clad Steel, C11000 Clad Steel from Copper Coated Steel Strps Brass

Model NO.
H90/F11/F18/H90
HS Code
721260000
Model NO.
H90/F11/F18/H90
HS Code
721260000
Copper-steel composite material with good elongation, high bonding strength, low resistivity, high tensile strength and low cost is provided. A copper-steel-copper composite material is disclosed. Its chemical composition proportion is 5-20% of copper and 80-95% of steel, and its structure is composed of copper and steel. The invention also discloses the preparation method of copper-steel composite material. The preparation steps are as follows: after surface treatment, copper and steel are rolled into high-precision steel strip and high-precision copper strip by cold rolling mill; after surface cleaning, surface residues are removed and degreased; high-precision copper-steel composite strip is rolled by cold rolling mill; and copper-steel composite strip is annealed at 650-850 C in vacuum furnace. In 1-4 hours, the structural molecules of the composite layer of two kinds of metal materials are melted, and then cooled to room temperature in vacuum furnace; the two kinds of strips are compounded to make the strips compounded into one and finish rolling; the composite materials are smoothed and polished, and the strips are packed after shearing according to the requirements of users.

Military industry: Copper-steel composite material temperature and pressure-penetration composite technology is a new technology emerging in the field of domestic metal composite strip materials, in addition to the high strength, good heat resistance, thermal stability, plasticity and corrosion resistance common to composite materials In addition to the characteristics of resistance and abrasion resistance, in the field of military bullet manufacturing, there are also the advantages of high yield and high dimensional accuracy, which are beneficial to improve the quality of bullets; the composite material has good consistency, thereby ensuring the consistency of the bullet and the shell; One batch is heavy and can be processed continuously, which greatly improves the production efficiency of bullets. The surface quality is excellent, comparable to pure copper; the brass on the surface of the copper-steel composite material also has a lubricating effect, which can reduce the impact on the barrel when shooting The wear and tear of the barrel and rim. It has been widely used in military products such as bullet shells and detonators. The sales network of military copper-steel composite materials has covered the world and won unanimous praise from many customers.
i)Military Products
Standard sizeBrass-steel-brassBrass-steel-brassBrass-steel-brass
Strip width139.5mm124/135/137/140mm< 600 mm
Strip thickness1.7-3.6mm0.5-1.37mm0.05-4.0 mm
Coating thickness3.4%-4%3.4%-4%3%-15 %
Base materialF18 steelF11 steelSPHC steel
Cladding materialH90 copperH90 copperH90 copper
Delivery formCoil / StripCoil / StripCoil / Strip
 

ii)Chemical Composition

 

Grade

 

Chemical composition of steel strip

C

Si

Mn

P

S

Ni

Cr

Cu

Als

%

%

%

%

%

%

%

%

%

F11

≤0.11

≤0.06

0.30-0.55

≤0.02

≤0.01

≤0.3

≤0.15

≤0.2

0.02-0.1

F18

0.11-0.19

≤0.06

0.35-0.55

≤0.02

≤0.01

≤0.3

≤0.15

≤0.2

0.02-0.1

SPHC

≤0.15

≤0.05

≤0.6

≤0.035

≤0.035

-

-

-

≥0.010

 

 

Grade

 

Chemical composition of copper strip

Cu+Ag

(min)

P

Bi

Sb

As

Fe

Pb

S

Zn

Total impurities

%

%

%

%

%

%

%

%

%

%

H90

88-91

-

-

-

-

≤0.1

≤0.02

-

allowance

≤0.2


iii)Mechanical properties and metallographic structure
 

 

material

tensile strength(Mpa)

Elongation(%)

Grain size

Pearlite

Non-metallic inclusionsA/B/C/D

Annealed

half hard

Annealed

half hard

H90/SPHC/H90

290~355

360~455

≥36%

≥8%

7-10

1-5

≤2.5

H90/F11/H90

265~365

-

≥43%

-

7-10

1-5

≤2.5

H90/F18/H90

305~395

-

≥37%

-

7-10

2-6

≤2.5

Copper Coated Steel Strps Brass



 