Low resistance copper nickel alloy 127 wire

Products

Low resistance copper nickel alloy 127 wire

China Low resistance copper nickel alloy 127 wire, Find details about China Alloy 127Wire, CuNi 127 from Low resistance copper nickel alloy 127 wire

Basic Info.

Model NO.

Alloy 127

Serves

Small Order Accepted

Sample

Sample Available

standard

GB/ASTM/JIS/BIS/DIN

Trademark

TANKII

Transport Package

According to Client′s Requirement

Specification

0.01-10mm

Origin

China

HS Code

74082200

Model NO.

Alloy 127

Serves

Small Order Accepted

Sample

Sample Available

standard

GB/ASTM/JIS/BIS/DIN

Trademark

TANKII

Transport Package

According to Client′s Requirement

Specification

0.01-10mm

Origin

China

HS Code

74082200

Product Desciption

Low resistance copper nickel alloy 127 wire
Material: CuNi1, CuNi2, CuNi6, CuNi8, cuni10, CuNi14, CuNi19, CuNi23, CuNi30, CuNi34, CuNi44. Manganin

Wire/Rod/Bar diameter: 0.02mm-30mm
Strip thickness: 0.1mm-5mm width: 5mm-200mm

Chemical Composition and Main Property of Cu-Ni Low Resistance Alloy
Properties\Grade		CuNi1	CuNi2	CuNi6	CuNi8	CuMn3	CuNi10
Main Chemical Composition	Ni	1	2	6	8	_	10
	Mn	_	_	_	_	3	_
	Cu	Bal	Bal	Bal	Bal	Bal	Bal
Max Continuous Service Temperature(ºC)		200	200	200	250	200	250
Resisivity at 20ºC (Ω*mm²/m)		0.03	0.05	0.1	0.12	0.12	0.15
Density(g/cm³)		8.9	8.9	8.9	8.9	8.8	8.9
Thermal Conductivity(α×10-6ºC)		<100	<120	<60	<57	<38	<50
Tensile Strength(Mpa)		≥210	≥220	≥250	≥270	≥290	≥290
EMF vs Cu(μVºC)(0~1000ºC)		-8	-12	-12	-22	_	-25
Approximate Melting Point(ºC)		1085	1090	1095	1097	1050	1100
Micrographic Structure		austenite	austenite	austenite	austenite	austenite	austenite
Magnetic Property		non	non	non	non	non	non

Properties\Grade		CuNi14	CuNi19	CuNi23	CuNi30	CuNi34	CuNi44
Main Chemical Composition	Ni	14	19	23	30	34	44
	Mn	0.3	0.5	0.5	1	1	1
	Cu	Bal	Bal	Bal	Bal	Bal	Bal
Max Continuous Service TemperatureºC)		300	300	300	350	350	400
Resisivity at 20ºC (Ω*mm²/m)		0.2	0.25	0.3	0.35	0.4	0.49
Density(g/cm³)		8.9	8.9	8.9	8.9	8.9	8.9
Thermal Conductivity(α×10-6ºC)		<30	<25	<16	<10	<0	<-6
Tensile Strength(Mpa)		≥310	≥340	≥350	≥400	≥400	≥420
EMF vs Cu(μVºC)(0~1000ºC)		-28	-32	-34	-37	-39	-43
Approximate Melting Point(ºC)		1115	1135	1150	1170	1180	1280
Micrographic Structure		austenite	austenite	austenite	austenite	austenite	austenite
Magnetic Property		non	non	non	non	non	non

Low resistance copper nickel alloy 127 wire

Low resistance copper nickel alloy 127 wire

Low resistance copper nickel alloy 127 wire

Low resistance copper nickel alloy 127 wire

Low resistance copper nickel alloy 127 wire

You Might Also Like