China FeCrAl alloy 0Cr27Al7Mo2 Alchrome Alloy Resistance Wire, Find details about China Alchrome Alloy Wire, Heating Wire from FeCrAl alloy 0Cr27Al7Mo2 Alchrome Alloy Resistance Wire
Chemical Composition and Main Property of Fe-Cr-Al Resistance Alloy | ||||||||
Properties \ Grade | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main Chemical Composition (%) | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Bal. | Bal. | Bal. | Bal. | Bal. | Bal. | Bal. | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max Continuous Service Temperature(oC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resisivity 20oC (Ω mm2/m) | 1.25 ± 0.08 | 1.42 ± 0.06 | 1.42 ± 0.07 | 1.35 ± 0.07 | 1.23 ± 0.07 | 1.45 ± 0.07 | 1.53 ± 0.07 | |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal Conductivity | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
(KJ/m@ h@ oC) | ||||||||
Coefficient of Thermal Expansion(α × 10-6/oC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Approximate Melting Point( oC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile Strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation(%) | > 16 | > 12 | > 12 | > 12 | > 12 | > 12 | > 10 | |
Section Variation | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Shrink Rate (%) | ||||||||
Repeatedly Bend Frequency(F/R) | > 5 | > 5 | > 5 | > 5 | > 5 | > 5 | > 5 | |
Hardness (H. B. ) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Continuous Service Time | no | ≥ 80/1300 | ≥ 80/1300 | ≥ 80/1300 | ≥ 80/1250 | ≥ 50/1350 | ≥ 50/1350 | |
Micrographic Structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic Property | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |