High Atmosphere Temperature Hn Apm Resistance Wire Used for Furnace Elements

China High Atmosphere Temperature Hn Apm Resistance Wire Used for Furnace Elements, Find details about China Apm Alloy Wire, Resistance Wire from High Atmosphere Temperature Hn Apm Resistance Wire Used for Furnace Elements

Basic Info.

Model NO.

APM

Hardness

220-260 Hv

Surface

Bright

Packing

Standard

Diameter

0.15-8.0mm

Flat Wire T

0.1-0.4mm

Flat Wire W

0.5-4.5mm

Flat Stirp T

0.5-2.5mm

Flat Stirp W

5-48mm

The Strength of 1000c

20 MPa

Trademark

Huona

Transport Package

Wooden Case, Wooden Pallet

Specification

0.5 ~ 10 mm, ISO9001, ISO14001

Origin

China

HS Code

85169090

Model NO.

APM

Hardness

220-260 Hv

Surface

Bright

Packing

Standard

Diameter

0.15-8.0mm

Flat Wire T

0.1-0.4mm

Flat Wire W

0.5-4.5mm

Flat Stirp T

0.5-2.5mm

Flat Stirp W

5-48mm

The Strength of 1000c

20 MPa

Trademark

Huona

Transport Package

Wooden Case, Wooden Pallet

Specification

0.5 ~ 10 mm, ISO9001, ISO14001

Origin

China

HS Code

85169090

Product Desciption

High atmosphere temperature APM Resistance Wire used for Furnace elements

This product takes refined master alloy as raw material, uses powder metallurgy technology to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat treatment process. The product has the advantages of strong oxidation resistance, good corrosion resistance at high temperature, small creep of electrothermal components, long service life at high temperature and small change of resistance. It is suitable for high temperature 1420 C, high power density, corrosive atmosphere, carbon atmosphere and other working environments. It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces, electronic industrial furnaces and diffusion furnaces.

Advantages
High atmosphere temperature Long life
High surface load Good oxidation resistance
Small proportion High resistivity
Good sulfur resistance

Specifications
Wire diameter range : φ0.1-8.5 mm

Flat Wire Thickness : 0.1-0.4 mm Width:0.5-4.5 mm

Flat Strip Thickness : 0.5-2.5 mm Width:5.0-48 mm

Main composition(Wt%)

	C	Si	Mn	Cr	Al	Fe
Min	-	-	-	20	5.5	Bal.
Max	0.04	0.5	0.4	22	6.0	Bal.

Main mechanical properties

Tensile Strength at Room Tmperature	Elongation	Hardness	Tensile Strength at 1000ºC	High Temperature Durability At 1000ºC and 6 Mpa
650-750 Mpa	15-25%	HV220-260	22-27Mpa	≥100h

Main physical properties