nichrome nikrothal 80 wire Heating Resistance Rod Cr20Ni80

Grade	Cr20Ni80
Size	10-60mm
Surface	oxidized/bright
Resistivity	1.04±0.05μΩ.m
Highest temperature	1100ºC
Density	7.9g/cm³
Tensile strength	750N/mm²
Elongation	≥20%

Grade	Highest temperature	Resistivity	Melting point	Tensile strength	Elongation
0Cr21Al4	1100ºC	1.23±0.06μΩ.m	1500ºC	750	≥12
0Cr25Al5	1250ºC	1.42±0.07μΩ.m	1500ºC	750	≥12
0Cr21Al6NbCo	1350ºC	1.43±0.07μΩ.m	1510ºC	750	≥12
0Cr27Al7Mo2	1400ºC	1.53±0.07μΩ.m	1520ºC	750	≥10
KSC	1350ºC	1.44±0.05μΩ.m	1510ºC	750	≥16
Cr20Ni80	1200ºC	1.09±0.05μΩ.m	1400ºC	750	≥20
Cr15Ni60	1150ºC	1.12±0.05μΩ.m	1390ºC	750	≥20
Cr20Ni35	1100ºC	1.04±0.05μΩ.m	1390ºC	750	≥20
Cr20Ni30	1100ºC	1.04±0.05μΩ.m	1390ºC	750	≥20

Grade	Chemical composition%
	C	P	S	Mn	Si	Cr	Ni	Al	Fe
	≤				Si	Cr	Ni	Al	Fe
0Cr21Al4	0.12	0.025	0.025	0.7	≤1.0	17-21	≤0.6	3-4	balance
0Cr25Al5	0.06	0.025	0.02	0.5	≤0.6	23-26	≤0.6	4.5-6.5	balance
0Cr21Al6Nb	0.05	0.025	0.02	0.5	≤0.6	21-23	≤0.6	5-7	balance
0Cr27Al7Mo2	0.05	0.025	0.02	0.2	≤0.4	26.5-27.8	≤0.6	6-7	balance
Cr20Ni80	0.08	0.02	0.015	0.6	0.75-1.6	20-23	balance	<0.5	≤1.0
Cr15Ni60	0.08	0.02	0.015	0.6	0.75-1.6	15-18	55-61	<0.5	balance
Cr20Ni35	0.08	0.02	0.015	1.0	1-3	18-21	34-37	-	balance
Cr20Ni30	0.08	0.02	0.015	1.0	1-3	18-21	30-34	-	balance

Recommend Produc
nichrome nikrothal 80 wire Heating Resistance Rod Cr20Ni80

Our main products include Iron chromium aluminum,nickel chromium two series products.Various types and specifications of resistance heatingwire,resistance strip products are widely used in industrial furnace,civil electrical appliances,rail transit braking resistor,central grounding resistance,automobile exhaust purification honeycomb carrier and other fields .