Tecwayhome 4.0mm Polymer Film Wet-Paved Waterproof Membrane (Double-Side Adhesive)

China Tecwayhome 4.0mm Polymer Film Wet-Paved Waterproof Membrane (Double-Side Adhesive), Find details about China Waterproof Material, Waterproof Membrane from Tecwayhome 4.0mm Polymer Film Wet-Paved Waterproof Membrane (Double-Side Adhesive)

Model NO.
TH-FL-WP40(DZ)
Function
Anti-static, Waterproof
Certification
ISO, CE
Color
Black
Usage
Outdoor, Indoor
Trademark
TECWAY
Transport Package
Pallets
Specification
7.5/10/15/20 sqm
Origin
China
HS Code
68071000
Model NO.
TH-FL-WP40(DZ)
Function
Anti-static, Waterproof
Certification
ISO, CE
Color
Black
Usage
Outdoor, Indoor
Trademark
TECWAY
Transport Package
Pallets
Specification
7.5/10/15/20 sqm
Origin
China
HS Code
68071000
 

Pre-Paved Waterproof Membrane

Tecwayhome 4.0mm Polymer Film Wet-Paved Waterproof Membrane (Double-Side Adhesive) 

Overview:

Pre-Paved Waterproof Membrane: composed of main material, self adhesive, surface anti adhesion (reducing) protective layer (except for membrane overlapping area) and isolation material (if necessary), which is bonded with post cast concrete to prevent water leakage on bonding surface.

 

Product Classification:

Pre-paved Waterproof Membrane

Main Material

Thickness of Membrane

Plastomer Waterproof Membrane (Type P)

1.2mm

1.5mm

1.7mm

Asphalt Base Polyester Waterproof Membrane (Type PY)

4.0mm

Rubber Waterproof Membrane (Type R)

1.5mm

2.0mm

 

Performance Index:

Executive Standard: GB/T23457-2017

No.

Items

Index

P

PY

R

1.

Soluble content /(g/m2) ≥

-

2900

-

2.

Tensile Properties

Tensile force / (N/50mm) ≥

600

800

350

Strength of Tensile/MPa

16

-

9

Rate of Film Elongation At Break /%  ≥

400

-

300

Elongation at Maximum Tensile Force /% ≥

-

40

-

Tensile Phenomena

No separation to rubber layer and polymer film or base

3.

Tearing Strength of Nail Rod /N  ≥

400

200

130

4.

Elastic Recovery Rate/%  ≥

-

-

80

5.

Puncture Resistance /N  ≥

250

550

100

6.

Impact Resistance (0.5kg.m)

No leakage

7.

Static Load Resistance

No leakage at 20kg

8.

Heat Resistance

80ºC, 2hr

No Dripping, No Sliding

70ºC, 2hr

No Dripping, No Sliding

100ºC, 2hr

No Dripping, No Sliding

9.

Cold Bending

No crack for main material at -35ºC

-

No crack for main material and rubber layer at -35ºC

10.

Low Temperature Flexibility / °C

No Cracks for rubber layer at -25ºC

No Cracks at -20ºC

-

11.

Oil Permeability / Number of sheets ≤

1

2

1

12.

Channeling Water Resistance (Hydraulic Gradient)

No running water for 0.8MPa/35min, 4h

13.

Impervious (0.3MPa, 120Min)

Impermeable

14.

Peeling Strength with Post-Cast Concrete (N/mm)

No Treatment 

1.5

1.5

0.8, cohesion damage

Soaking Treatment

1.0

1.0

0.5, cohesion damage

Sediment Contaminated Surface

1.0

1.0

0.5, cohesion damage

Ultraviolet Treatment

1.0

1.0

0.5, cohesion damage

Heat Treatment

1.0

1.0

0.5, cohesion damage

15.

Peeling Strength with Post-Cast Concrete After Immersion /(N/mm) ≥

1.0

1.0

0.5, cohesion damage

16.

Peel Strength Between Membrane and Membrane / (N/mm) ≥

No Treatment 

0.8

0.8

0.6

Soaking Treatment

0.8

0.8

0.6

17.

Peel Strength of Anti-Sick Treatment Part of Membrane /(N/mm)

0.1 or non-sticky

18.

.Thermal Aging (80°C, 168hr)

Tensile Retention Rate /% ≥

90

80

Elongation Retention Rate /% ≥

80

70

Cold Bending

No cracks of main material at -32°C

-

No cracks of main material at -32°C

Low Temperature Flexibility

No cracks of rubber layer at -23°C

No cracks at -18°C

-

19.

Dimensional change / % ≤

±1.5

±0.7

±1.5

 Tecwayhome 4.0mm Polymer Film Wet-Paved Waterproof Membrane (Double-Side Adhesive)Tecwayhome 4.0mm Polymer Film Wet-Paved Waterproof Membrane (Double-Side Adhesive)