Hot pure copper foil E-Copper

China Hot pure copper foil E-Copper, Find details about China Copper Foil, Pure Copper Foil from Hot pure copper foil E-Copper

Basic Info.

Model NO.

E-copper

Standard

GB/T

Sample

Small Order Accept

surface

bright

Serves

Small Order Accepted

colour

RED

Trademark

Tankii

Transport Package

in Roll, Wooden Case Outside

Specification

GB/T5231-2001

Origin

China

HS Code

74101100

Model NO.

E-copper

Standard

GB/T

Sample

Small Order Accept

surface

bright

Serves

Small Order Accepted

colour

RED

Trademark

Tankii

Transport Package

in Roll, Wooden Case Outside

Specification

GB/T5231-2001

Origin

China

HS Code

74101100

Product Desciption

High Technology Copper Manganin Shunt Resistor for Kwh Meter

Cu%99.90 C11000 Cu ETP
Min thickness:0.001mm
little order can accept
Specification of red copper strip we supply:
Strip: thick:0.15-3.0mm width:610mm
Plate:thick:0.5-3mm width:610mm Length:2500mm

With the assistance of our advanced technology, we offer quality range of Copper Strips and Plate. Manufactured using finest grade of raw material our array is widely used in numerous industries for excellent finish, corrosion resistance and durability. We even custom design these strips and flats as per client specific requirement.

Quality ltems		General Technical Terms
Quality ltems		1/3 OZ/ft 2 (12μ m)	1/2 OZ/ft 2 (18μ m)	3/4OZ/ft 2 25μ m	1 OZ/ft 2 35μ m	7/5 OZ/ft 2 (1.4μ m)	2 OZ/ft 2 (70μ m)
Area Weight(g/)		102-112	153	230	305	435	610
Tensile Strenght(kg/mm 2)	STD-E	≥ 205	≥ 205	≥ 235	≥ 275	≥ 275	≥ 275
Tensile Strenght(kg/mm 2)	HD-E	≥ 17	≥ 103	≥ 156	≥ 205	≥ 205	≥ 205
Elongation(%)	STD-E	≥ 2	≥ 205	≥ 3	≥ 3	≥ 3	≥ 3
Elongation(%)	HD-E	≥ 2	≥ 2.5	≥ 3	≥ 3	≥ 5	≥ 5
Surface Roughness(μ m)	Shiny Surface Ra	≤ 0.43	≤ 0.43	≤ 0.43	≤ 0.43	≤ 0.43	≤ 0.43
Surface Roughness(μ m)	Matte Surface Rz	5	6	10	10	12	12
Peel Strength(Kg/cm)		≥ 1.1	≥ 1.2	≥ 1.8	≥ 1.8	≥ 2.1	≥ 2.1
Leakage Poins(points/)		≤ 5			No
High Temperature Anti-Oxidization Performance		Treat in the 200 constant temperature for 60 minutes, there is no oxidation stain