China Customized High Precision Al203 Alumina Ceramic Tube Ceramic Part Ceramic Rack for Photovoltaic Machinery Parts, Find details about China Ceramic, Zirconia Ceramic from Customized High Precision Al203 Alumina Ceramic Tube Ceramic Part Ceramic Rack for Photovoltaic Machinery Parts
Attribute | Zirconia | Alumina | ZTA |
Density | 5.9-6.05g/cm3 | 3.6-3.8g/cm3 | 4.8g/cm3 |
Hardness(HRC) | 88-90 | 80-86 | 86 |
Fracture Toughness | 10MPa.m½ | 4MPa.m½ | - |
Compressive Strength | 2000MPa | 1500MPa | 1700MPa |
CTE | 10.5ppm/ºC | 7.15-7.67ppm/ºC | 9.1ppm/ºC |
Maximum Operating Temperature | 1350ºC | 1700ºC | 1350ºC |
Thermal Conductivity(24ºC) | 2W/m.k | 18-28W/m.k | - |
Flexural Strength (24ºC) | 950MPa | 300MPa | 600MPa |
Water Absorption(%) | 0 | 0 | 0 |