Nickel silver flat Wire/Ribbon /Square Wire 2.0*7.0mm

China Nickel silver flat Wire/Ribbon /Square Wire 2.0*7.0mm, Find details about China Nickel Silver strip, Copper Nickel alloy from Nickel silver flat Wire/Ribbon /Square Wire 2.0*7.0mm

Basic Info.

Model NO.

CuNi18Zn20

Size

T:0.01-5mm

surface

bright

standard

GB/ASTM/JIS/BIS/DIN

Sample

Small Oreder Accepted

Density

8.9(g/cm3)

state

Soft 1/4hard 1/2hard hard T-hard

Trademark

TANKII

Transport Package

500m/Spool

Specification

0.01-3mm*0.3-600mm

Origin

Shanghai, China

HS Code

7409400000

Model NO.

CuNi18Zn20

Size

T:0.01-5mm

surface

bright

standard

GB/ASTM/JIS/BIS/DIN

Sample

Small Oreder Accepted

Density

8.9(g/cm3)

state

Soft 1/4hard 1/2hard hard T-hard

Trademark

TANKII

Transport Package

500m/Spool

Specification

0.01-3mm*0.3-600mm

Origin

Shanghai, China

HS Code

7409400000

Product Desciption

Nickel silver flat Wire/Ribbon /Square Wire 2.0*7.0mm

Product Description

Categories: High precision copper alloy strip & plate

Name: High performance zinc copper nickel alloy strip & plate

Number: C75200

Feature: Elasticity modulus: 115GPa

Good fatigue resistance.

Good electroplate performance

Welding performance is good

Fastness in high temperature

Good cold working, deep drawing, curve performance.

Articles,Chemical composition

Articles				Chemical composition
GB	UNS	EN	JIS	Cu%	Ni%	Zn%
BZn18-26	C77000	CuNi18Zn27	C7701	54-58	16.5-19.5	Rem

Physical properties,fabrication properties

Physical properties					fabrication properties
density g/cm3	electrical conductivity %IACS	thermal conductivity W/(m.K)	modulus of elasticity GPa	specific heat J/(g.K)	cold- workability	electric plating property	hot dip tin plating property	weldability
8.7	5	32	125	0.34	excellent	excellent	excellent	good

Mechanical properties

Mechanical properties
State	Hardness HV	Tension test				bending(in rolling direction)rest			bending(transverse to rolling direction)test
		thickness mm	tensile strength MPa	yield strength MPa	elon gation %	THS mm	angles	ID	THS mm	angles	ID/T
1/2H	150-210	0.1-0.7	540-655	≥390	≥8	≤1.6	180°	150%	≤0.5	180°	300%
		≥0.71	540-655	≥390	≥11
H	180-240	0.1-0.7	630-735	≥390 ≥500	≥4	≤1.6	180°	200%	≤0.5	180°	400%
		≥0.71	630-735	≥500	≥6
EH	210-260	≥0.1	705-805	≥600	-	≤1.6	90°	300%	≤0.5	90°	600%
SH	230-270	≥0.1	765-865	≥680	-	-	-	-	-	-	-

Typical application

Shields,Liquid crystal oscillators

Articles,Chemical composition

Articles				Chemical composition
GB	UNS	EN	JIS	Cu%	Ni%	Zn%
BZn18-18	C75200	CuNi18Zn20	C7521	62-66	16.5-19.5	Rem

Physical properties,fabrication properties

Physical properties					fabrication properties
density g/cm3	electrical conductivity %IACS	thermal conductivity W/(m.K)	modulus of elasticity GPa	specific heat J/(g.K)	cold-work ability	machin ability	electric plating property	hot dip tin plating property	weld ability
8.73	6	32	125	0.34	excellent	suitable	excellent	excellent	good

Mechanical properties

Mechanical properties
State	Hardness HV	Tension test			bending test
		Thickness mm	Tensile strength MPa	elongation %	thickness	angles	ID
0	-	0.1-5.0	≥375	≥20	≤1.6	180°	sticking closely
1/2H	120-180	0.1-5.0	440-570	≥5	≤1.6	180°	100% of thickness
					≤0.5		200% of thickness
H	150-210	0.1-0.15	540-640	-	≤1.6	180°	200% of thickness
		>0.15-5.0		≥3	≤0.5		400% of thickness
EH	≥185	0.1-5.0	≥610	-	-	-

Typical application

Shields,Liquid crystal oscillators,pressing parts

Articles,Chemical composition

Articles				Chemical composition
GB	UNS	EN	JIS	Cu%	Ni%	Zn%
BZn15-20	C75400	CuNi15Zn20	C7541	60-64	12.5-15.5	Rem

Physical properties,fabrication properties

Physical properties					fabrication properties
density g/cm3	electrical conductivity %IACS	thermal conductivity W/(m.K)	modulus of elasticity GPa	specific heat J/(g.K)	cold-workability	machin ability	electric plating property	hot dip tin plating property	weld ability
8.7	6	32	135	0.34	excellent	suitable	excellent	excellent	good

Mechanical properties

Mechanical properties
State	Hardness HV	Tension test			bending test
State	Hardness HV	Thickness mm	Tensile strength MPa	elongation %	thickness	angles	ID
0	-	0.1-5.0	≥355	≥20	≤1.6	180°	sticking closely
1/2H	110-170	0.1-5.0	410-540	≥5	≤1.6	180°	100% of thickness
H	≥135	0.1-0.15	≥490	-	≤1.6	180°	200% of thickness
H	≥135	>0.15-5.0	≥490	≥3	≤1.6	180°	200% of thickness