China AR/ARG Glassfibre Chopped Strand for GFRC, Find details about China Gfrc Chopped Strand, Grc Chopped Strand from AR/ARG Glassfibre Chopped Strand for GFRC

Model NO.
ARC13-76-12MMH ZrO2 16.7%
Trademark
HUIERJIE
Origin
China
HS Code
70191200
Model NO.
ARC13-76-12MMH ZrO2 16.7%
Trademark
HUIERJIE
Origin
China
HS Code
70191200
HUIERJIE ZRO2 16.7% Premix is a high integrity chopped fibre, designed for using in dry mix systems or other premixing processes for subsequent molding into a GRC intricate component.
HUIERJIE ZRO216.7% High integrity has a low-tex strand which permits efficient reinforcement at low dosages. The coating size systems give easy incorporation whilst retaining best strand integrity, especially used in the electric closet panels.
HUIERJIE ZRO2 16.7% water dispersed can be simply added to the mix at the workshop without the need of a special equipment and disperse into filaments in a matrix of calcium silicate slurry, cement slurry etc.
Application:
The 'Premix' production technique involves pouring or pumping a cement/fibre mix into a mould, similar to other precast production processes. The mix is compacted using vibration or by adding other components. The unit is left in mould to set and demoulded the following day.Pre-mix has the advantages that moulds can be simper to produce and strip
PREMIX   CODEHIGH INTERGRITY CODEWATER DISPERSED
ARC13-76-12MMH
ARC15-98-12MMH		ARC11-40-12MMHARC13-76-12MMHD
ARC15-98-12MMHD
 
Technical Data
  • Type of glass                       Alkali Resistant      (AR)       
  • Zirconia (ZrO2) content                 ≥16.7%
  • Filament diameter um                   13+2  11+2  15+2
  • Strand tex                              76+8  40+5  98+10
  • Elastic modulus                           80.4 Gpa                     
  • Tensile strength                            1.7 Gpa
 
  • Length avaiable(MM)                    6/12/18/20/24/30/36
  • Moisture Content                       ≤0.2%
  • Sizing Content                             0.8 - 2.0%
  • Breaking strength                      ≥0.32 N/tex
 
BENEFITS
Excellent alkali resistant and durability
Highest integrity during mix
Good fluidity
Been approved by Sheffied University,UK
 
Packaging&Storage
20kgs /kraft bag, 40bags/800Kg/pallet/109*109*105cm; 50bags /109*109*125cm,20palltes/ 1*20' FCL, N.W.18ton.
Huierjie AR Glassfibre roving pallet shall be stored dry in original packaging and advisable to stack in one layer, at a temperature between 15ºC- 35ºC & relative humidity between 35%- 65%.If stored below 15ºC, it is advisable to hold in workshop for 24 hours to prevent condensation before use.
 
 
Note:
Huierjie ARG Fiber are manufactured with high Zirconia rate in compliance with the BSEN 15422:2008 and ASTM C1666/C 1666/M-07 and under the recommendations of GRCA
 