Closed Cell PU Polyurethane Spray Foam Raw Materials for Building Insulation

China Closed Cell PU Polyurethane Spray Foam Raw Materials for Building Insulation, Find details about China "Polyurethane Rigid Foam, Polyether Polyol from Closed Cell PU Polyurethane Spray Foam Raw Materials for Building Insulation

Model NO.
SDA13E
Gel Time
100-120s
Rise Time
100-120s
Physical Properities
35~46kg/M3
Compressive Strength
200~300kpa
Trademark
shunda
Transport Package
220kg/Drum
Specification
Two components
Origin
China
HS Code
39072090
Model NO.
SDA13E
Gel Time
100-120s
Rise Time
100-120s
Physical Properities
35~46kg/M3
Compressive Strength
200~300kpa
Trademark
shunda
Transport Package
220kg/Drum
Specification
Two components
Origin
China
HS Code
39072090
Blend Polyol SDA13E
Spray Rigid PU Foam For Cold storage
DESCRIPTION
SDA13E cold storage insulation system blend polyol is a kind of spray rigid PU foam blend polyol, specially used for the insulation of the wall of storage insulation. It used together with isocyanate(PM-200) to make rigid PU foam through PU spray machine. The foam produced has the characteristics as following:
  1. The strong adhesive force, convenient construction and no seams.
  2. The low thermal conductivity, low water absorption and good dimensional stability.
  3. The long service life.
TYPICAL PHYSICAL PROPERTIES
Physical ProperitiesTest MethodMetricValue
Core DensityGB/T 6343-2009kg/m345.3
Compressive StrengthGB/T 8813-2008kPa264
Tensile StrenghtGB/T 9641-88kPa136
Oxygen indexGB/T 2406.2-2009 %23.4
Initial Thermal ConductivityGB/T 10294-2008W/(m·K)0.022
Close Cell ContentGB/T 10799-2008%≥88
Water AbsorptionGB/T 8810-2005%≤3
Dimensional Stability
(Foam made After 6 days)		-25ºCGB/T 8811-2008%≤±1
≤±1
70ºC
Importance: The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.

Other unmentioned matters and TDS&MSDS.Please visit our official website shundapu.en.made-in-china.com
Or please contact us for information:
 
 
------------------------------------------------------------------
DESCRIPTION
SD1133 cold storage insulation system blend polyol is a kind of spray rigid PU foam blend polyol, specially used for the insulation of the wall of storage insulation. It used together with isocyanate(PM-200) to make rigid PU foam through PU spray machine. The foam produced has the characteristics as following:
  1. The strong adhesive force, convenient construction and no seams.
  2. The low thermal conductivity, low water absorption and good dimensional stability.
  3. The long service life.
TYPICAL PHYSICAL PROPERTIES
Physical ProperitiesTest MethodMetricValue
Core DensityGB/T 6343-2009kg/m345.3
Compressive StrengthGB/T 8813-2008kPa264
Tensile StrenghtGB/T 9641-88kPa136
Oxygen indexGB/T 2406.2-2009 %23.4
Initial Thermal ConductivityGB/T 10294-2008W/(m·K)0.022
Close Cell ContentGB/T 10799-2008%≥88
Water AbsorptionGB/T 8810-2005%≤3
Dimensional Stability
(Foam made After 6 days)		-25ºCGB/T 8811-2008%≤±1
≤±1
70ºC
Importance: The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.
COMPONENT PRODUCT SPECIFICATIONS
PropertyBlend polyol 
SD1133		Polymeric      MDI Pm200
AppearancePale yellow liquid.Brown liquid
Specific gravity at 25°C1.10±0.10 g/cm31.22-1.25 g/cm3
Viscosity at 25°C300±100 cps200±50 cps
Shelf life3 months12 months
REACTIVITY PROFILE
Cream TimeGel TimeRise Time
0-1 s2-3 s4-6 s

INSTALLATION GUIDELINE
SD1133Ambient TemperaturesSpraying TemperaturesMinimum Spray Pressures
Summer10-35ºC35-41ºC5516kPa (800 psi)
Sping~Autumn0-15ºC35-45ºC5516kPa (800 psi)
Winter-10-5ºC35-50ºC5516kPa (800 psi)
SD1133:PM200=1:1(volume ratio)
 Foaming Machine:Polyurethane Rigid foam Spray Machine
ADDITIONAL INFORMATION
  1. Maximum per pass thickness is 35mm,Spraying thicker can result in spontaneous combustion and poor overall spray foam quality
  2. Internal temperature of installed pass must be 25ºC before installing subsequent passes Maximum thickness during 24h period is 203mm(8inches)
  3. Like most of foam product,foam made by SD1133is combustible,An thermal barrier must be installed in accordance with approved construction standards SD1133
  4. The service temperature of the foam with SD1133 is between -60~80ºC.
PACKING SPECIFICATION 
220KGS/Drum, Blue paint or Zinc coating drums (Drum Weight: 18-23kg)
STORAGE RECOMMENDATIONS  
The blend polyol should be stored in the sealed container to avoid the absorption of water vapor.  During the transportation, it should avoid serious shake and strong sunlight. It should be stored in ventilated place, avoiding light, water and fire. Recommended storage temperature is 15~25ºC.
Shelf life: 6 months, please test before using after 6 months storage.

Closed Cell PU Polyurethane Spray Foam Raw Materials for Building Insulation
Closed Cell PU Polyurethane Spray Foam Raw Materials for Building Insulation
Closed Cell PU Polyurethane Spray Foam Raw Materials for Building Insulation

Closed Cell PU Polyurethane Spray Foam Raw Materials for Building Insulation
 

You Might Also Like