China Aqueous Acrylic Polymer Emulsion Resin for Waterborne Acrylic Lacquer, Find details about China Chemical Wall Putty, Wall Paint from Aqueous Acrylic Polymer Emulsion Resin for Waterborne Acrylic Lacquer
Silicone modified acrylate emulsion----HN-519T | ||
HN-519T | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 100-1000 | |
Particle Size(nm) | 90-160 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -40ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |
HN-101 | Appearance | Light blue liquid |
Solid content | 47±2wt% | |
Viscosity.Cps(25ºC) | 1000-4000cps | |
Particle Size(nm) | 90-150 | |
PH | ||
Glass Transition Temperature (Tg) | 26ºC | |
Minimum Film Formation Temperature(MFT) | 22-24ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-102 | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 500-3000 | |
Particle Size(nm) | 100-180 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 24ºC | |
Minimum Film Formation Temperature(MFT) | 21-23ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-996 | Appearance | Light blue liquid |
Solid content | 49±1wt% | |
Viscosity.Cps(25ºC) | 500-3000 | |
Particle Size(nm) | 90-150 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 22ºC | |
Minimum Film Formation Temperature(MFT) | 18-20ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-4208A | Appearance | Translucency and light blue liquid |
Solid content | 46±2wt% | |
Viscosity.Cps(25ºC) | 3000-6000 | |
Particle Size(nm) | 60-100 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 23ºC | |
Minimum Film Formation Temperature(MFT) | 22ºC | |
HN-4208 | Appearance | Translucency and light blue liquid |
Solid content | 42±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 90-120 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 7-10ºC | |
HN-01F | Appearance | Light blue liquid |
Solid content | 29±1wt% | |
Viscosity.Cps(25ºC) | ≤500cps | |
Particle Size(nm) | 80-120 | |
PH | 7.5-8.5 | |
Minimum Film Formation Temperature(MFT) | 10ºC | |
HN-314T | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 100-500 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -15ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-519NT | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 100-1000 | |
Particle Size(nm) | 90-160 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -40ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-340T | Appearance | Milk white liquid |
Solid content | 56±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 300-400 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-332T | Appearance | Milky white with a hint of green |
Solid content | 56±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 200-300 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |