China Styrene Polymer Acrylic Resin Emulsion for Sale, Find details about China Acrylic Emulsion Water Based, Water Based Acrylic Emulison from Styrene Polymer Acrylic Resin Emulsion for Sale
Silicone modified acrylate emulsion----HN-314T | ||
HN-314T | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 100-500 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -15ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |
HN-101 | Appearance | Light blue liquid |
Solid content | 47±2wt% | |
Viscosity.Cps(25ºC) | 1000-4000cps | |
Particle Size(nm) | 90-150 | |
PH | ||
Glass Transition Temperature (Tg) | 26ºC | |
Minimum Film Formation Temperature(MFT) | 22-24ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-102 | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 500-3000 | |
Particle Size(nm) | 100-180 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 24ºC | |
Minimum Film Formation Temperature(MFT) | 21-23ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-996 | Appearance | Light blue liquid |
Solid content | 49±1wt% | |
Viscosity.Cps(25ºC) | 500-3000 | |
Particle Size(nm) | 90-150 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 22ºC | |
Minimum Film Formation Temperature(MFT) | 18-20ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-4208A | Appearance | Translucency and light blue liquid |
Solid content | 46±2wt% | |
Viscosity.Cps(25ºC) | 3000-6000 | |
Particle Size(nm) | 60-100 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 23ºC | |
Minimum Film Formation Temperature(MFT) | 22ºC | |
HN-4208 | Appearance | Translucency and light blue liquid |
Solid content | 42±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 90-120 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 7-10ºC | |
HN-01F | Appearance | Light blue liquid |
Solid content | 29±1wt% | |
Viscosity.Cps(25ºC) | ≤500cps | |
Particle Size(nm) | 80-120 | |
PH | 7.5-8.5 | |
Minimum Film Formation Temperature(MFT) | 10ºC | |
HN-314T | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 100-500 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -15ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-519NT | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 100-1000 | |
Particle Size(nm) | 90-160 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -40ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-340T | Appearance | Milk white liquid |
Solid content | 56±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 300-400 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-332T | Appearance | Milky white with a hint of green |
Solid content | 56±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 200-300 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |