Addition Cure Silicone Molding for Statues
China Addition Cure Silicone Molding for Statues, Find details about China Addition Cure Silicone, Silicone Rubber from Addition Cure Silicone Molding for Statues
Basic Info.
Model NO.
902-40, 902-30, H8225, H8230
Trademark
XD silicone
Specification
10KG, 20KG, 40KG, 50KG
Origin
Beijing
HS Code
3910000000
Model NO.
902-40, 902-30, H8225, H8230
Trademark
XD silicone
Specification
10KG, 20KG, 40KG, 50KG
Origin
Beijing
HS Code
3910000000
Product Desciption
Appilications:
1. sculpture, cement / gypsum product, architectural and furniture elements
2. resin crafts, casting wax, art objects
Features:
High temperature resistance, acid and alkali-resistance, aging resistance.
Low shrinkage, high hardness and no-deformation
High tensile and tear strength, easy to de-molding
Technical data sheet:
How to use:
1.A and B must be mixed evenly into a clean plastic or metal container, The bottom and walls of the container must be scraped well to ensure that the silicone is mixed with the curing agent.
2.The pre-operation time of the mixed is 30-40 minutes at room temperature, and the product prototype is poured by vacuum defrosting.The product can be cured completely at room temperature of 3-4 hours and heated at 80-120ºC for 30 minutes.
3. When pouring or brushing mold for medium or large products, it is recommended to pour or brush 2-3mm thick silica gel on the surface of the product to fully and completely contact with the prototype.
4.At 25ºC, A/B is fully mixed and stored safely for 30-40 minutes.The higher the temperature, the shorter the storage time.
Package: 10KG, 20KG, 25KG, 200KG or according to customer requirements.
1. sculpture, cement / gypsum product, architectural and furniture elements
2. resin crafts, casting wax, art objects
Features:
High temperature resistance, acid and alkali-resistance, aging resistance.
Low shrinkage, high hardness and no-deformation
High tensile and tear strength, easy to de-molding
Technical data sheet:
| Model | 902-40 | 902-30 | H8225 | H8230 |
| Mixing ratio (A:B) | 100:2~3 | 100:2~3 | 1:1 | 1:1 |
| Hardness (Shore A)≥ | 25 | 30 | 25 | 30 |
| Tear-strength (kgf/c m²)≥ | 21 | 22 | 25 | 26 |
| Viscosity ( mixed 25°C mpa.S) | 25000±2000 | 25000±2000 | 18000±2000 | 20000±2000 |
| Shrinkagerate (%)≤ | 0.2 | 0.2 | 0.1 | 0.1 |
| Elongation(%) | 450 | 400 | 450 | 400 |
How to use:
1.A and B must be mixed evenly into a clean plastic or metal container, The bottom and walls of the container must be scraped well to ensure that the silicone is mixed with the curing agent.
2.The pre-operation time of the mixed is 30-40 minutes at room temperature, and the product prototype is poured by vacuum defrosting.The product can be cured completely at room temperature of 3-4 hours and heated at 80-120ºC for 30 minutes.
3. When pouring or brushing mold for medium or large products, it is recommended to pour or brush 2-3mm thick silica gel on the surface of the product to fully and completely contact with the prototype.
4.At 25ºC, A/B is fully mixed and stored safely for 30-40 minutes.The higher the temperature, the shorter the storage time.
Package: 10KG, 20KG, 25KG, 200KG or according to customer requirements.
You Might Also Like
Shangyan Men′ S Pure Cotton Solid Color Slim Fit Casua......
Engine Spare Parts 13511-38011 13511-35010 22r Camshaft for ......
Original Perkin Alternator Charger Spare Part Maintenance Pa......
Factory Custom Made 3D Antique Copper Plated Metal Badge Man......
Lottery Machine by Air Mixing with Large Capacity
Cross Beauty Back Shockproof Gather Fitness Vest Skin-Friend......
245/ 35r19 UHP Tire Passenger Car Tire SUV Tire
Hospital Equipment Optometry Equipment Titanium Ophthalmic B......
CNC Aluminum Profile Machining Center
Optical Fiber Cable with 4 Core
New Carton Forming Machine Automatic Case Erector From Shand......
China Factory Supply Natural Colorants Marigold Flower Extra......