China Polystyrene PS Resin/HIPS/GPPS/EPS Granules Plastic Raw Material, Find details about China Polystyrene PS Resin, HIPS Granules from Polystyrene PS Resin/HIPS/GPPS/EPS Granules Plastic Raw Material
Polystyrene (PS) granules: is composed of styrenemonomer (SM) polymerization, can be synthesized by a variety of synthetic methods, the current industry mainly by bulk polymerization and suspension polymerization.
Polystyrene(PS) is a thermoplastic non-crystalline resin, mainly divided into General Purpose polystyrene (GPPS), High Impact polystyrene (HIPS) and Expandable Polystyrene (EPS) .
1. Polystyrene foam (Expanded Polystyrene referred to as EPS) is a light-weight polymer. It is the use of polystyrene resin into the blowing agent, while heating to soften, produce gas,forming a hard closed-cell structure foam Plastic.
2.Impact resistant polystyrene (HIPS) is an impact resistant polystyrene product produced by adding polybutyl rubber particles to polystyrene.
1. High Impact Polystyrene(HIPS)
HIPS can be used to produce the shells of electrical household appliances, toys, automobile parts, daily necessities, etc. HIPS has excellent impact resistance, rigidity,electrical insulating property, corrosion resistance and dyeability.
2. General purpose polystyrene (GPPS)
GPPS, can be used for daily necessities, electrical appliances, instrument housings, toys, lamps, household appliances, stationery, cosmetics containers, indoor and outdoor decorations, fruit plate, optical parts (such as prism, lens) lens and molding, Lamps, telecommunications accessories, electric frequency capacitors film, high-frequency insulation materials, television sets and other containers, waveguide, chemical containers.ade is mainly used for making rotomolded products, large-sized outdoor toys, storage tanks, roadblocks, etc.
3. Expandable polystyrene (EPS)
EPS has also been used for a large number of decorative materials, film and television scene layout, character modeling, marine life jackets and buoys. In particular, large foam sheet market demand is very large, as color steel sandwich panel, steel (board) grid composite light panels, wall outside the paste board, roof insulation boards and geothermal panels, it is more widely Used in the field of housing construction, for insulation, heat insulation, waterproof and moisture-proof materials on the ground.
Item | Test conditions | Test method | Test data | unit |
Density | ISO 1183:1987 | 1040 | kg/m3 | |
Water absorption | ISO 62:1999 | <0.1 | % | |
Melt flow rate | 200ºC/5kg | ISO 1133:1997 | 3.8 | cm3/10min |
Process shrinkage | ISO 294-4:1997 | 0.4-0.6 | % | |
Charpy impact strength | 1eU | ISO 179:1993 | 15 | kj/m2 |
Tensile modulus | 1mm/min | ISO 527-2:1993 | 3300 | MPa |
Elongation | 50mm/min | ISO 527-2:1993 | 3 | % |
Tensile strength at break | 50mm/min | ISO 527-2:1993 | 55 | MPa |
Ball indentation hardness H | 358N/30s | ISO 2039-1:1993 | 150 | N/mm2 |
Bending strength | 2mm/min | ISO 178:1993 | 100 | MPa |
HDT | 1.8MPa | ISO 75-2:1993 | 84 | ºC |
Linear coefficient of thermal expansion | (23-80)ºC | DIN 53 752 | 0.8-1.0 | K-1 |
Heat conduction | DIN 52 612 | 0.16 | W/mK | |
Vicat softening point | B50/oil | ISO 306:1994 | 93 | ºC |
Flame retardance | >1.4mm | UL-Standard 94 | 94HB | Class |
1.Packing:
25kg/bag, or per your requirement.
18-20mt/20'FCL
2.Storage:
The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air.
3.Transportation:
During transportation, the product should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.