Products

High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes

China High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes, Find details about China High Density Graphite, Carbon Graphite Provider from High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes

Density
1.91-1.95 g/cm3
Electrical Resistivity
11-13
Flexural Strength
No Less Than 60 MPa
Compressive Strength  MPa
More Than135
Thermal Conductivity
85W/M*K
Trademark
L. T graphite
Transport Package
Cartons in Wooden Cases
Specification
personalized customized
Origin
Cn
HS Code
3801909000
Density
1.91-1.95 g/cm3
Electrical Resistivity
11-13
Flexural Strength
No Less Than 60 MPa
Compressive Strength  MPa
More Than135
Thermal Conductivity
85W/M*K
Trademark
L. T graphite
Transport Package
Cartons in Wooden Cases
Specification
personalized customized
Origin
Cn
HS Code
3801909000

 

Company Profile
 
High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes
As a proud subsidiary of L.T Group, L.T Graphite with four producing bases located at middle of China, Henan province, and a branch producing base at Sichuan province. L.T graphite covers the entire value chain of fine and medium grain graphite production. From raw material selection, semi-finished product manufacture, precision machining, impregnation, purification, and coating. This is how we ensure the consistent high quality and performance of our products.
 

 

Product Description
High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes
Graphite rotor is mainly used in liquid aluminum, aluminum alloy purification process, to improve the purity of aluminum or aluminum alloy. It is the most advanced treatment method in the world that mix the purification gas and solvent, use the rotating jet of the graphite rotor to purify the aluminum during the purification process,                         
Under high temperature aerobic conditions, in the production process of on - line degassing machine for fine aluminum casting, graphite rotor has defects of easy  oxidation & break, no friction. Our team choose high quality reasonable ratios of graphite materials, coated with high temperature antioxidants which was R&D independently while no pollution to the Aluminum liquid. Our unique anti-oxidant graphite rotor performs outstanding oxidation resistance, corrosion resistance, high hardness, high compressive strength makes continuous use for 90-120 days available, thus effectively reduce producing cost for customers.
Working principle
High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes
A twirling graphite rotor shatters nitrogen (or argon), which is blown into melting aluminum, into profuse bubbles that disperse in the liquid metal. Regarding gas pressure difference and surface adsorption principle, bubbles in the melt absorb hydrogen and oxidation slag inclusion which are taken out to surface of the melt with the rise of the bubbles, so that the melt can be purified.
 
Working conditions
High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes
Working conditions:
Put the impeller end and part of the shaft of a graphite rotor into 690°C-780°C Aluminum liquid, rotation speed  500 RPM, 1-2 hours at a time, work for 4-6 times per day. graphite rotor can also work continuously according to the working condition of the equipment.
 

 

Product Parameters
High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes
High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes

 

Product features
High Strength Impregnated Phenolic Graphite Resin Rotors and Vanes
1. Our graphite rotor is made of high-quality graphite material.
2. After special anti-oxidant treatment, the service life could reach 5 -10 times compared to ordinary market graphite rotor.
3. Our graphite rotor widely used in high purity aluminum industry and aluminum alloy casting industry.

 

 









 

 