CuNi10 Low Resistance Alloy Wire

China CuNi10 Low Resistance Alloy Wire, Find details about China CuNi10 Wire, CuNi10fe1mn from CuNi10 Low Resistance Alloy Wire

Basic Info.

Model NO.

CuNi10(alloy 90)

Trademark

Tankii

Origin

China

HS Code

74082200

Model NO.

CuNi10(alloy 90)

Trademark

Tankii

Origin

China

HS Code

74082200

Product Desciption

CuNi10 Low Resistance Alloy Wire

Material: CuNi1, CuNi2, CuNi6, CuNi8, CuNi14, CuNi19, CuNi20, CuNi23, CuNi25, CuNi30, CuNi34, CuNi44.
Wire/Rod/Bar diameter: 0.02mm-30mm
Strip: Thickness0.01~6.0width: 610Max
CuNi10, also known as Cuprothal 15, is a copper-nickel alloy (CuNi alloy) with medium-low resistivity for low temperature resistances. The alloy is suitable for use at temperatures up to 400°C (750°F).
CuNi10 is typically used for heating cables, fuses, resistors and various types of controllers.

Material: CuNi10(C70600) CuNi30(C71500) in from of sheet/plate/strip

CuNi10Fe1/C70600 Strip/sheet
Copper Nickels (Copper-Nickel), Copper-Nickel, (90-10). Excellent corrosion resistance, especially in marine environments. Moderately high strength, good creep resistance at elevated temperatures. Properties generally increase with nickel content. Relatively high in cost compared with copper-aluminum and other alloys with similar mechanical propert

Characteristic	Resistivity ( 200C μ Ω . m)	Max. working Temperature ( 0C)	Tensile Strength (Mpa)	Melting point (0C)	Density ( g/cm3)	TCR x10-6/ 0C (20~600 0C)	EMF vs Cu (μ V/ 0C) (0~100 0C)
Alloy Nomenclature
NC035(CuNi30)	0.35± 5%	300	350	1150	8.9	< 16	-34

Mechanical Properties	Metric	Comments
Tensile Strength, Ultimate	372 - 517 MPa
Tensile Strength, Yield	88.0 - 483 MPa	Depending on temper
Elongation at Break	45.0 %	in 381 mm.
Modulus of Elasticity	150 GPa
Poissons Ratio	0.320	Calculated
Charpy Impact	107 J
Machinability	20 %	UNS C36000 (free-cutting brass) = 100%
Shear Modulus	57.0 GPa