China High Transpancy Clear Epoxy Resin for SLA 3D Printing, Find details about China Clear Epoxy Resin, Resin Expoxy from High Transpancy Clear Epoxy Resin for SLA 3D Printing
PHYSICAL CHARACTERISTICS ( LIQUID STATE ) | Resin Appearance: White Density: 1.13 g/cm³@25ºC Viscosity: 355 CPS@28ºC Dp: ≥0.145 mm Ec: 9.3 mJ/cm² | |
MOLDING PERFORMANCE A @355nm point laser@150mW power@10.0m/s scanning@No UV post-cure | Appearance: White Flexural Modulus: 2692~2775MPa Flexural Strength: 69-74 Impact strength notched lzod: 27~31 J/m 1.2mm Bend Angle140~170° | |
MOLDING PERFORMANCE B MOLDING PERFORMANCE @90min UV post-cure | Tensile Modulus: 2189~2395 MPa Tensile Strength: 27~31 MPa Notched Impact Strength40~55 J/m Hardness: 83 Elongation at break: 12~20% Heat deflection temperature: 52 ºC Glass transition temperature, Tg: 62 ºC Coefficient of thermal expansion: 97*E-6 |
PHYSICAL CHARACTERISTICS ( LIQUID STATE ) | Resin Appearance: Brown Density: 1.11-1.15 g/cm³@25ºC Viscosity: 405-500 CPS@28ºC Dp: ≥0.135-0.152 mm Ec: 8.9-9.5 mJ/cm² | |
MOLDING PERFORMANCE A @355nm point laser@150mW power@10.0m/s scanning@No UV post-cure | Appearance: Brown Flexural Modulus: 2682~2778MPa Flexural Strength: 70-74 Impact strength notched lzod: 30~37 J/m 1.2mm Bend Angle140~170° | |
MOLDING PERFORMANCE B MOLDING PERFORMANCE @90min UV post-cure | Tensile Modulus: 2599~2715 MPa Tensile Strength: 40~58 MPa Hardness: 77-88 Elongation at break: 7~12% Heat deflection temperature: 55-68ºC Glass transition temperature, Tg: 60-75 ºC Coefficient of thermal expansion: 90-102*E-6 |
PHYSICAL CHARACTERISTICS ( LIQUID STATE ) | Resin Appearance: light yellow Density: 1.11-1.15 g/cm³@25ºC Viscosity: 450-530 CPS@28ºC Dp: ≥0.14-0.16mm Ec: 7.1-8.1 mJ/cm² | |
MOLDING PERFORMANCE A @355nm point laser@150mW power@10.0m/s scanning@No UV post-cure | Appearance: Yellow Flexural Modulus: 2685~2775MPa Flexural Strength: 71-78 Impact strength notched lzod: 25~40 J/m 1.2mm Bend Angle140~170° | |
MOLDING PERFORMANCE B MOLDING PERFORMANCE @90min UV post-cure | Tensile Modulus: 2611~2765 MPa Tensile Strength: 45~58 MPa Hardness: 78-90 Elongation at break: 13~22% Heat deflection temperature: 55-69ºC Glass transition temperature, Tg: 60-79 ºC Coefficient of thermal expansion: 85-99*E-6 |