Two Parts Mix Liquid Cloudy Silicone Rubber for Plaster Molds with Crafts Silicon Glue
China Two Parts Mix Liquid Cloudy Silicone Rubber for Plaster Molds with Crafts Silicon Glue, Find details about China Two Parts Molding Silicone Rubber, Liquid Molds Making Silicone from Two Parts Mix Liquid Cloudy Silicone Rubber for Plaster Molds with Crafts Silicon Glue
Basic Info.
Model NO.
HY-625
Viscosity
Adjustable
Shelf Life
12 Months
Type of Company
Factory
Trademark
HongYe
Transport Package
20kg/Drum
Origin
China
HS Code
39100000
Model NO.
HY-625
Viscosity
Adjustable
Shelf Life
12 Months
Type of Company
Factory
Trademark
HongYe
Transport Package
20kg/Drum
Origin
China
HS Code
39100000
Product Desciption
Description two parts mix Liquid cloudy Silicone Rubber for Plaster Molds with Crafts silicon glue
HY-625 is a kind of room temperature vulcanized silicone rubber in condensation type. It's generally named as two part silicone rubber , Part A is a flowable liquid, part B is the curing agent or catalyst . It's mainly used for mold making .
Application two parts mix Liquid cloudy Silicone Rubber for Plaster Molds with Crafts silicon glue
HY-625 silicone rubber is used for making molds of concrete stone,GRC, gypsum decoration , plaster ornaments, fiberglass products, polyester decoration, unsaturated resin crafts, polyresin crafts, polyurethane, bronze, wax, candle, and similar products .
HY-625 Silicone rubber is with good fluidity and moderate hardness which is suitable for middle size product with pattern by pouring operation, especially popular for manufacturer of resin crafts and gypsum decoration . Besides ,additive is available for brushing operation.It's one of our best selling silicone !
Technical Parameters
Characteristics two parts mix Liquid cloudy Silicone Rubber for Plaster Molds with Crafts silicon glue
*An exceptional fluidity and good operability, easy to demold
*Moderate hardness
*High tensile and tear strength
*Good flexibility
*Cure at room temperature
*Outstanding bubble releasing
*High duplication times
Operation instructions
Step 1: prepare the original molds
Make sure your original molds perfect. fix it on a board. And fix the original mold on a board , then used four piece of board to enclose the original molds .
Step 2: Take 100 G parts A and add 2G parts B and mix them evenly.
*Notes: Mold making silicon rubber is a kind of flowing liquid ,it contains two parts. Part A is a kind of flowing white liquid and part B is the curing agent or catalyst .Pls follow the step strictly:
1.Weigh the two part exactly by electronic weight..
If not , for example add two much catalyst , the operation time will be too fast to operate ,which will cause inconvinience to operate .
2.Mix part A and part B evenly.
Otherwise the silicon rubber will be partly solidified and this will give birth to difficulties in your final operation. What's more, the finished molds will meet a short life. All of these will cause a waste of silicon rubber.
Step 3: Vacuum pumping
Without exception, this step takes less than 1 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available.
Step 4: Pouring casting or Brush operation
*Notes:1. For simple pattern products we suggest use pouring operation way , which will be very easy to operate and demould. Pourable silicone require light viscosity which will be easy to flow smoothly and easy to de-air .
2.For delicate pattern products we suggest use brushing operation way , which can copy the pattern exactly . Brushable silicone require high viscosity which won't be easy to flow away and easy to brush .
3. We sugges to set the silicone mold for another 12 hours after demould before put into large production .
The proportions and reactions of the curing agent and the silicon are listed as follows:
1. Adding curing agent 1%, the silicone can still be operated within 2.5 hours and can be demoulded after 6-8 hours.
2. Adding curing agent 2%, the silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.
3. Adding curing agent 3%, the silicone can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.
Package
25KG/drum vacuum packing for part A +1kg/ bottle catalyst for part B
200KG/drum packing for part A +1kg/ bottle catalyst for part B
Shelf life
1, Long history and solid foundation
With 21 years of development history and good reputation, our products are exported to 138 countries around the world and exported since 2006.
2, High-end research and development (free sample)
Being a leading liquid silicone manufacturer(6000 square meter factory )
in China, we have a professional R&D team and QC team(12 experts ) and our product is FDA, SGS, RoHS, MSDS, ISO, REACH, UL approved, so there is no need to worry about the quality.And we have 14 years on alibaba.com, 12 years on made-in-china.com, a trustworthy company
3, Efficient service
We can provide free training of silicone technique and free silicone samples. we have a professional sales team who will solve your problems patiently. Besides, with efficient logistics distribution system, you could get you goods earlier. Last, good after-sales service,we build long term cooperation relationship, once there is quality problem, we could solve right away. More importantly, return and exchange are accepted while quality problems occurred
Please do not hesitate in contacting me should you require any further assistance. Lisa will be happy to help.(Free Sample)
Mobile/ Whatsapp/: +86 189 3886 7508
HY-625 is a kind of room temperature vulcanized silicone rubber in condensation type. It's generally named as two part silicone rubber , Part A is a flowable liquid, part B is the curing agent or catalyst . It's mainly used for mold making .
Application two parts mix Liquid cloudy Silicone Rubber for Plaster Molds with Crafts silicon glue
HY-625 silicone rubber is used for making molds of concrete stone,GRC, gypsum decoration , plaster ornaments, fiberglass products, polyester decoration, unsaturated resin crafts, polyresin crafts, polyurethane, bronze, wax, candle, and similar products .
HY-625 Silicone rubber is with good fluidity and moderate hardness which is suitable for middle size product with pattern by pouring operation, especially popular for manufacturer of resin crafts and gypsum decoration . Besides ,additive is available for brushing operation.It's one of our best selling silicone !
Technical Parameters
| Model | Color | Mixing ratio (%) | Pot life (mins, under 25ºC) | Curing time (hrs,under 25ºC ) | Hardness ( Shore A ) | Tensile- strength (MPa) | Tear- strength (kN/m) | Viscosity (After A/B mixed ,mPa.s) | Shrinkage rate (%) | Elongation (%) |
| HY-625 | White /translucent | 2-3 | 30-40 | 4-5 | 25±2 | 4.8±0.5 | 29±2 | 27000±5000 | ≤0.3% | 500% |
Characteristics two parts mix Liquid cloudy Silicone Rubber for Plaster Molds with Crafts silicon glue
*An exceptional fluidity and good operability, easy to demold
*Moderate hardness
*High tensile and tear strength
*Good flexibility
*Cure at room temperature
*Outstanding bubble releasing
*High duplication times
Operation instructions
Step 1: prepare the original molds
Make sure your original molds perfect. fix it on a board. And fix the original mold on a board , then used four piece of board to enclose the original molds .
Step 2: Take 100 G parts A and add 2G parts B and mix them evenly.
*Notes: Mold making silicon rubber is a kind of flowing liquid ,it contains two parts. Part A is a kind of flowing white liquid and part B is the curing agent or catalyst .Pls follow the step strictly:
1.Weigh the two part exactly by electronic weight..
If not , for example add two much catalyst , the operation time will be too fast to operate ,which will cause inconvinience to operate .
2.Mix part A and part B evenly.
Otherwise the silicon rubber will be partly solidified and this will give birth to difficulties in your final operation. What's more, the finished molds will meet a short life. All of these will cause a waste of silicon rubber.
Step 3: Vacuum pumping
Without exception, this step takes less than 1 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available.
Step 4: Pouring casting or Brush operation
*Notes:1. For simple pattern products we suggest use pouring operation way , which will be very easy to operate and demould. Pourable silicone require light viscosity which will be easy to flow smoothly and easy to de-air .
2.For delicate pattern products we suggest use brushing operation way , which can copy the pattern exactly . Brushable silicone require high viscosity which won't be easy to flow away and easy to brush .
3. We sugges to set the silicone mold for another 12 hours after demould before put into large production .
The proportions and reactions of the curing agent and the silicon are listed as follows:
1. Adding curing agent 1%, the silicone can still be operated within 2.5 hours and can be demoulded after 6-8 hours.
2. Adding curing agent 2%, the silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.
3. Adding curing agent 3%, the silicone can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.
- Adding curing agent 4%, the silicone can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.
Package
25KG/drum vacuum packing for part A +1kg/ bottle catalyst for part B
200KG/drum packing for part A +1kg/ bottle catalyst for part B
Shelf life
- Twelve(12) months when stored under dry and cool place by original package under 25ºC
1, Long history and solid foundation
With 21 years of development history and good reputation, our products are exported to 138 countries around the world and exported since 2006.
2, High-end research and development (free sample)
Being a leading liquid silicone manufacturer(6000 square meter factory )
in China, we have a professional R&D team and QC team(12 experts ) and our product is FDA, SGS, RoHS, MSDS, ISO, REACH, UL approved, so there is no need to worry about the quality.And we have 14 years on alibaba.com, 12 years on made-in-china.com, a trustworthy company
3, Efficient service
We can provide free training of silicone technique and free silicone samples. we have a professional sales team who will solve your problems patiently. Besides, with efficient logistics distribution system, you could get you goods earlier. Last, good after-sales service,we build long term cooperation relationship, once there is quality problem, we could solve right away. More importantly, return and exchange are accepted while quality problems occurred
Please do not hesitate in contacting me should you require any further assistance. Lisa will be happy to help.(Free Sample)
Mobile/ Whatsapp/: +86 189 3886 7508
You Might Also Like
FDA Approved Lemborexant Sleep-Wake Disorders and Insomnia D......
Dmr Digital Two-Way Radio, UHF/VHF, Compatible with Mototrbo......
Multifunctional Shr Opt/RF Hair Removel Elight Birth Mark Re......
Air Lift D2300 2300lbs Rubber Air Spring Bag for Car Truck A......
Hot Feed Rubber Extruder with Ce
Single Girder Gantry Crane with Factory Price
D2w6y Cheap Manual Home Used ABS Crank Hospital Foldaway Bed
Old Style Wooden Treasure Box with Brass Latch Woodcraft
Arena PARA Gatos for Toilet Bentonite Cat Sand Pet Supply
Women A Line Short Knee Length Tutu Tulle Prom Party Skirt
G Single Screw Progressive Cavity Pump Self-Priming Slurry P......
700ml Round Shape Spirits Vodka Whisky Brandy Glass Bottle