Refractory Ceramic Needled Blanket

China Refractory Ceramic Needled Blanket, Find details about China Ceramic Blanket, Ceramic Needled Blanket from Refractory Ceramic Needled Blanket

Model NO.
Thickness: 20mm, 25mm, 30mm, 50mm
Surface Finishing
Matt
Edge
Square
Shape
Square
Refractory Temperature
1200 Degree
Usage
Building, Baking
Feature
Long Time Materials
Trademark
KT
Transport Package
Carton
Origin
China
HS Code
6806900000
Model NO.
Thickness: 20mm, 25mm, 30mm, 50mm
Surface Finishing
Matt
Edge
Square
Shape
Square
Refractory Temperature
1200 Degree
Usage
Building, Baking
Feature
Long Time Materials
Trademark
KT
Transport Package
Carton
Origin
China
HS Code
6806900000
Aluminosilicate Refractory Fiber needled blanket is produced from fiber wool which is made into wool blanket by certain method, and followed by mechanically-needled reinforcement process for required thickness and cutting process for proper sizes to packed.

Bulk density is 128-220kg/m3.

It's widely used in the furnace linning for industry furnace, thermal insulation for high temperature tube, filtrating,
Type
Property
STD
Standard
HP
High  Purity
HA
High  Alumina
ZA
Zirconia
ZAC
Chromia
ST
Mircrolite
Working  temperature degree C< 1000< 1100< 1200< 1350< 1400< 1250
Color
White

White

White

White

Glaucous

White
(μ m)
Average  Fier  Diameter
3-52-52-42-42-32-4
(mpa)128kg/m3
Tensile  Strength
0.040.0350.030.0250.030.025
degree C× 24h
Heating  permanent  line  changes
1150≤ 41260≤ 41350≤ 41350≤ 41400≤ 41250≤ 4
± 15% kg/m3
Bulk  Density
96-12896-128160-18096-16096-160160-180
w/m@ k
Thermal  Conductivity  at  Average  Temperature              128kg/m3              160kg/m3
400 degree C0.09    0.080.07    0.060.08    0.060.09    0.090.090.08    0.06
6000.13    0.110.10    0.080.11    0.080.13    0.130.130.11    0.08
8000.2    0.150.15    0.140.15    0.090.21    0.170.180.15    0.09
10000.24    0.210.20    0.170.21    0.120.25    0.22   0.250.21    0.13
% Typical  Chemical  Composition
Al2O3≥ 4545-4753-55≥ 35≥ 4353-55
Al2O3+SiO2> 96> 99> 99> 99> 99> 99
ZrO2___15.6__
Fe2O3< 1.2< 0.2< 0.2< 0.2< 0.2< 0.2
CrO2    3