Water Base Styrene Acrylic Resin Coating for Building Decoration

China Water Base Styrene Acrylic Resin Coating for Building Decoration, Find details about China Chemical, Wall Paint from Water Base Styrene Acrylic Resin Coating for Building Decoration

Basic Info.

Model NO.

HN-01F

Method

Brush

Level

Primer

Drying Method

Drying

Certification

ISO14001, CCC, RoHS, ISO9001

Substrate

Ceramic

Components

Auxiliaries

Formation Mechanism

Non Conversion Type

Application

Primer for The Internal and External Walls

Solid Content

29+/-1wt%

Viscosity.Cps

<=500cps

Particle Size

80-120nm

7.5-8.5

Film Formation Temperature

10 Centigrade

Trademark

Transport Package

Plastic Barrel

Specification

1 Ton

Origin

China

HS Code

3906909000

Model NO.

HN-01F

Method

Brush

Level

Primer

Drying Method

Drying

Certification

ISO14001, CCC, RoHS, ISO9001

Substrate

Ceramic

Components

Auxiliaries

Formation Mechanism

Non Conversion Type

Application

Primer for The Internal and External Walls

Solid Content

29+/-1wt%

Viscosity.Cps

<=500cps

Particle Size

80-120nm

7.5-8.5

Film Formation Temperature

10 Centigrade

Trademark

Transport Package

Plastic Barrel

Specification

1 Ton

Origin

China

HS Code

3906909000

Product Desciption

Water base styrene acrylic resin coating for building decoration

^{Product description:}

As a general purpose primer for the internal and external walls . The acrylate emulsion has excellent wet adhesion, permeability and alkali resistance.

Feature:

1.Excellent wet adhesion
2.Good alkali resistance
3.Good permeability
4.Short drying time

Water Base Styrene Acrylic Resin Coating for Building Decoration

^{Silicone modified acrylate emulsion----HN-01F}
HN-01F	Appearance	Light blue liquid
	Solid content	29±1wt%
	Viscosity.Cps(25ºC)	≤500cps
	Particle Size(nm)	80-120
	PH	7.5-8.5
	Minimum Film Formation Temperature(MFT)	10ºC
	Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification.	Pass

Application:

As a general purpose primer for the internal and external walls

^{Vinyl acetate-acrylate emulsion catalog:}

HN-101	Appearance	Light blue liquid
	Solid content	47±2wt%
	Viscosity.Cps(25ºC)	1000-4000cps
	Particle Size(nm)	90-150
	PH
	Glass Transition Temperature (Tg)	26ºC
	Minimum Film Formation Temperature(MFT)	22-24ºC
	Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification.	Pass
HN-102	Appearance	Light blue liquid
	Solid content	48±1wt%
	Viscosity.Cps(25ºC)	500-3000
	Particle Size(nm)	100-180
	PH	7.0-8.0
	Glass Transition Temperature (Tg)	24ºC
	Minimum Film Formation Temperature(MFT)	21-23ºC
	Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification.	Pass
HN-996	Appearance	Light blue liquid
	Solid content	49±1wt%
	Viscosity.Cps(25ºC)	500-3000
	Particle Size(nm)	90-150
	PH	7.0-8.0
	Glass Transition Temperature (Tg)	22ºC
	Minimum Film Formation Temperature(MFT)	18-20ºC
	Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification.	Pass
HN-4208A	Appearance	Translucency and light blue liquid
	Solid content	46±2wt%
	Viscosity.Cps(25ºC)	3000-6000
	Particle Size(nm)	60-100
	PH	7.0-8.0
	Glass Transition Temperature (Tg)	23ºC
	Minimum Film Formation Temperature(MFT)	22ºC
HN-4208	Appearance	Translucency and light blue liquid
	Solid content	42±1wt%
	Viscosity.Cps(25ºC)	1000-3000
	Particle Size(nm)	90-120
	PH	7.0-8.0
	Minimum Film Formation Temperature(MFT)	7-10ºC
HN-01F	Appearance	Light blue liquid
	Solid content	29±1wt%
	Viscosity.Cps(25ºC)	≤500cps
	Particle Size(nm)	80-120
	PH	7.5-8.5
	Minimum Film Formation Temperature(MFT)	10ºC
HN-314T	Appearance	Light blue liquid
	Solid content	48±1wt%
	Viscosity.Cps(25ºC)	1000-3000
	Particle Size(nm)	100-500
	PH	7.0-8.0
	Glass Transition Temperature (Tg)	-15ºC
	Minimum Film Formation Temperature(MFT)	0ºC
	Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification.	Pass
HN-519NT	Appearance	Light blue liquid
	Solid content	48±1wt%
	Viscosity.Cps(25ºC)	100-1000
	Particle Size(nm)	90-160
	PH	7.0-8.0
	Glass Transition Temperature (Tg)	-40ºC
	Minimum Film Formation Temperature(MFT)	0ºC
	Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification.	Pass
HN-340T	Appearance	Milk white liquid
	Solid content	56±1wt%
	Viscosity.Cps(25ºC)	1000-3000
	Particle Size(nm)	300-400
	PH	7.0-8.0
	Minimum Film Formation Temperature(MFT)	0ºC
	Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification.	Pass
HN-332T	Appearance	Milky white with a hint of green
	Solid content	56±1wt%
	Viscosity.Cps(25ºC)	1000-3000
	Particle Size(nm)	200-300
	PH	7.0-8.0
	Minimum Film Formation Temperature(MFT)	0ºC
	Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification.	Pass

Our company:

Shandong Honour Chemical Technology Co.,Ltd, located in the middle of Shandong Peninsula.Honour is a collection of science, industry, trade, storage, logistics, R & D, humanities education, financing, financial services integration of the comprehensive high-tech enterprises.
Honour specilze in the operation of acrylate and its extended products.The annual production capability of the environmentally waterborne acrylic emulsion, auxiliaries and waterborne polyurethane dispersions can reach to 600,000 Tons, and there are 16,000 tons chenmical liquid storage tank and 10,000 square meters solid storage in the factory.Newbetta is the largest acrylate product supplier in Shandong, with 25,000 tons production capacity of waterborne paint, waterborne metaphysical paint and other terminal products.