China Cr12W flat bar/1.2436/Cr12W/DIN 1.2436 / AISI D6 Cold Work Tool Steel/Flat Bar/Steel Block/Round Bar, Find details about China Tool Steel AISI D6, AISI D6 AISI D6 Steel from Cr12W flat bar/1.2436/Cr12W/DIN 1.2436 / AISI D6 Cold Work Tool Steel/Flat Bar/Steel Block/Round Bar
DIN 1.2436 / AISI D6 Cold Work Tool Steel
DIN 1.2436 / AISI D6 Cold Work Tool Steel is used for making cutting and drawing tools of high wear resistance, rolls with high dimensional stability, deep drawing tools, tools of wire, bar and tube production, cold shear blades for thin sheets.
Dimensions
Flat: 6-120 x 40-810 mm
Delivery Condition
EAF+(ESR) or EAF+LF+VD+(ESR), Hot rolled or Forged, Annealed, Black surface or Machined surface, UT SEP1921 Class3 D/d
Equivalence
AISI / SAE | DIN / W.Nr | JIS | GB |
D6 | 1.2436 | ---- | Cr12W |
Chemical Composition(%)
Steel Grade | C | Si | Mn | P | S | Cr | W |
1.2436 | 2.00-2.30 | 0.10-0.40 | 0.30-0.60 | ≤ 0.030 | ≤ 0.030 | 11.00-13.00 | 0.60-0.80 |
D6 | 2.00-2.20 | 0.70-0.90 | 0.20-0.40 | ≤ 0.030 | ≤ 0.030 | 11.50-12.50 | 0.60-0.90 |
Cr12W | 2.00-2.30 | ≤ 0.40 | ≤ 0.40 | ≤ 0.030 | ≤ 0.030 | 11.50-13.00 | 0.60-0.80 |
Charecteristics
1. A kind of cold work tool steel with excellent wear resistance and edge holding ability
2. High surface hardness after heat treatment.
3. Medium toughness, but high compressive strength, and good through hardening properties and dimensional stability.
Heat Treatment
Annealing
800 to 850°C
Slow con trolled cooling in furnace at a rate of 10 to 20°C/hr down to approx. 600°C, further cooling in air.
Hardness after annealing: max. 250 HB
Stress relieving
650 to 700°C
Slow cooling in furnace; intended to relieve stresses set up by extensive machining, or incomplex shapes.
After through heating, hold in neutral atmosphere for 1 to 2 hours.
Hardening
950 to 980°C
Oil, salt bath (220 to 250°C or 500 to 550°C), air plast, still air. Holding time after temperature equalization: 15 to 30 minutes. Obtainable hardness: 64 - 66 HRC.
Special treatment: Hardening 1020°C and tempering at 500°C.
Obtainable hardness approx. 61 HRC (e.g. if followed by nitriding).
Tempering
Slow heating to tempering temperature immediately after hardening/time in furnace 1 hour for each 20 mm of workpiece thickness but at least 2 hours/cooling in air. For certain cases we recommend to reduce tempering temperature and increase holding time.