Tungsten carbide alloy grade:

Size: dia0.3-60mm
Length: 5-600mm
WC Grain size range: 0.3~0.5μ.m; 0.5~0.9μ.m; 1.0~1.3μ.m; 1.4~2.0μ.m
Tungsten carbide alloy --
1. High hardness after quenching and tempering 
2. Excellent wear resistance
3. Excellent hot-work performance
Tungsten carbide Copper Composite Features:
No Fe, Co, Ni, Mn and other elements added as the sintering activator, to maintain a high thermal conductivity
Excellent hermeticity
Can provide semi-finished or finished (Ni/Au plated) products
Precision machining and excellent dimensional control, surface finish and flatness
With close technical support including product design, custom manufacturing, testing and post sale supports.

1. Pure tungsten rod Specification:
Surface:Black and polished
Purity:≥99.95%
Density:≥19.2g/cm3,
Surface roughness:<1.6
Dia:2.5-120mm
2. Pure tungsten rod surface finish:
Black: surface is as swaged or as drawn, retaining a ciating of processing lubricants and oxides.
Cleaned: Surface is chemically cleaned to removed all lubricants and oxides.
Ground: Surface is centerless to ground to remove all coating and to achieve precise diameter control.



Tungsten alloy rod:
1.Material: W90-97NiFe(Magnetic) & W90-97NiCu(Nonmagnetic)
2.Density:16.8-18.8g/cm3
3.Size:
   rod dia(1.5 -200) x Length300mm  Plate: 0.1min Thickness*W*L

4.Property of tungsten alloy

AMST 21014 class 1
90%WNiFe, 90%WNiCu
Density : 17.0
Hardness: 32HRC max
Elongation: 5-20%

AMST 21014 class 2
92.5%WNiFe, 92.5%WNiCu
Density : 17.2
Hardness: 33HRC max
Elongation: 5-15%

AMST 21014 class 3
95%WNiFe, W95NiCu
Density : 18.0
Hardness: 34HRC max
Elongation: 3-10%

AMST 21014 class 4
97.5%WNiFe, W97.5NiCu
Density : 18.85
Hardness: 35HRC max
Elongation: 1-8%