Centrifugal Casting Aluminum Steel Winding Spool for Cold Rolling Mill to Produce Aluminum Foils

China Centrifugal Casting Aluminum Steel Winding Spool for Cold Rolling Mill to Produce Aluminum Foils, Find details about China Steel Winding Spool, Steel Bushing from Centrifugal Casting Aluminum Steel Winding Spool for Cold Rolling Mill to Produce Aluminum Foils

Basic Info.

Model NO.

as the drawing

Material

Alloy

Application

Metal Processing Machinery Parts

Application Range

Aluminum Foils,Plates and Stainless Foils&Plates

Trademark

FANGLE

Transport Package

Seaworthy Package

Specification

as the requirement

Origin

China

Model NO.

as the drawing

Material

Alloy

Application

Metal Processing Machinery Parts

Application Range

Aluminum Foils,Plates and Stainless Foils&Plates

Trademark

FANGLE

Transport Package

Seaworthy Package

Specification

as the requirement

Origin

China

Product Desciption

Centrifugal Casting Aluminum Steel Winding Spool for Cold Rolling Mill

Description
Centrifugal casting steel sleeve,also called casting steel bushing, is one of the main spare parts used for cold rolling mill. The centrifugal casting process is dedicated to ensure internal and external surfaces of sleeve have no defects such as crack, slag, blowhole, blister, etc. The heat treatment process will make sure the mechanical performance of sleeve. With the special machining tool and rational process the sleeves have high performance of concentricity, cylindrical, symmetry and balancing.

Performance:

Materail	strength of extension(MPa)	Yield strength(MPa)	ductility(%)	hardness(HB)
ZG310-570	570	310	≥ 17	217-255
35CrMo	≥985	≥835	≥ 12	≥229
35CrMoV	≥1080	≥930	≥ 10	≥240
35NiCrMo	≥830	≥660	≥ 8	≥240
KCP-12	≥1080	≥835	≥ 8	240-260

Chemical material:

Material	C	Si	Mn	Cr	Ni	Mo	V	S,P	illustration
ZG310 -570	0.50	0.60	0.90					<=0.040	Low plasticity and toughness, poor high temperature resistance, Low purchasing cost
35CrMo	0.32 - 0.40	0.17 - 0.37	0.40 - 0.70	0.80 - 1.1		0.15 - 0.25		≤0.035	High strength, toughness and hardenability, General high temperature resistance Low purchasing cost
35CrMoV	0.30 - 0.38	0.17 - 0.37	0.40 - 0.70	1.00 - 1.30		0.20 - 0.30	0.10 - 0.20	≤0.035	Slightly better than 35CrMo, Can meet the general use requirements, Economical purchasing cost
35NiCrMo	0.30 - 0.37	0.60 - 0.90	0.70 - 1.00	0.40 - 0.90	0.60 - 0.90	0.40 - 0.50		<=0.035	High strength and toughness , good high temperature resistance, high purchasing cost