Melt volume-flow rate | 300 °C; 1.2 kg | cm³/10 min | ISO 1133 | 2.0 |
Molding shrinkage, parallel | 60x60x2 mm; 500 bar | % | ISO 294-4 | 0.75 |
Molding shrinkage, normal | 60x60x2 mm; 500 bar | % | ISO 294-4 | 0.8 |
Melt mass-flow rate | 300 °C; 1.2 kg | g/10 min | ISO 1133 | 2.5 |
Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 2300 |
Yield stress | 50 mm/min | MPa | ISO 527-1,-2 | 64 |
Yield strain | 50 mm/min | % | ISO 527-1,-2 | 6.6 |
Nominal strain at break | 50 mm/min | % | ISO 527-1,-2 | > 50 |
Stress at break | 50 mm/min | MPa | ISO 527-1,-2 | 65 |
Strain at break | 50 mm/min | % | b.o. ISO 527-1,-2 | 100 |
Flexural modulus | 2 mm/min | MPa | ISO 178 | 2300 |
Flexural strength | 2 mm/min | MPa | ISO 178 | 94 |
Flexural strain at flexural strength | 2 mm/min | % | ISO 178 | 7.2 |
Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178 | 70 |
Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | N |
Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | N |
Charpy impact strength | -60 °C | kJ/m² | ISO 179-1eU | N |
Charpy notched impact strength | 23 °C; 3 mm | kJ/m² | ISO 7391/b.o. ISO 179-1eA | 75P |
Charpy notched impact strength | -30 °C; 3 mm | kJ/m² | ISO 7391/b.o. ISO 179-1eA | 20C(P) |
Izod notched impact strength | 23 °C; 3 mm | kJ/m² | ISO 7391/b.o. ISO 180-A | 65P |
Izod notched impact strength | -30 °C; 3 mm | kJ/m² | ISO 7391/b.o. ISO 180-A | 55P(C) |
Puncture maximum force | 23 °C | N | ISO 6603-2 | 5500 |
Puncture maximum force | -30 °C | N | ISO 6603-2 | 6400 |
Puncture energy | 23 °C | J | ISO 6603-2 | 55 |
Puncture energy | -30 °C | J | ISO 6603-2 | 60 |
Ball indentation hardness | N/mm² | ISO 2039-1 | 108 |