PC Resin, Polycarbonate Resin Plastic Raw Material

China PC Resin, Polycarbonate Resin Plastic Raw Material, Find details about China PC Resin, Polycarbonate from PC Resin, Polycarbonate Resin Plastic Raw Material

Sample
Avaiable
Grade
Injection
Glass Fiber
5%-60%
Shape
Pellets, Granules, Particle
Trademark
TOPO NEW
Transport Package
25kgs/Bag
Specification
65*40*15cm
Origin
China
HS Code
390740000
Sample
Avaiable
Grade
Injection
Glass Fiber
5%-60%
Shape
Pellets, Granules, Particle
Trademark
TOPO NEW
Transport Package
25kgs/Bag
Specification
65*40*15cm
Origin
China
HS Code
390740000

PC Resin,Polycarbonate Resin plastic raw material

PC Resin, Polycarbonate Resin Plastic Raw Material
GF Reinforced PC compound material is usually filled with 5%-30% glass fiber as a reinforcing agent.

After combination, the compound material has excellent toughness, strength, stress crack resistance, high hardness, and heat resistance. It is also dimensionally stable and is able for spray.  

Materials can meet ROHS environmental requirements, and they are widely used in electronic components, bearing cages, gears, parts and components, automotive parts, and so on. TOPO NEW MATERIAL can provide reliable customized services according to clients' specific requirements.
PC(C010203 NA)
 Product Description Applications
· Good dimensional stability· Injection molding
·  Excellent heat stability· Good mechanical properties balance
 Properties Test Method Test Condition  UnitTypical Values
Physical properties
Specific Gravity ISO 118323ºC g/cm31.2
MIISO 1183 g/10min3
Ash ISO 3451800ºC,30min % 0
Mechanical properties
Tensile Strength ISO 527 50mm/min MPa 72
(yield) elongationISO 527 50mm/min %120
Flexural Modulus ISO 1782mm/min MPa 2300
Cantilever beam notched impact strength ISO18023ºCKJ/m275
Non-notched impact strength of cantilever beamISO17923ºCKJ/m282
Thermal properties
Heat deflection temperatureISO 751.80MPa°C129
Melting PointDSC-C 
Other properties
Flammability UL943.2 V2
Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. Prior to use the material, please consult with TOPO NEW  Material Co., Ltd.
 Processing Conditions Range 
Melt Temperature304-327ºC
Mold Temperature82.2-121ºC
Pre-Dry needed121ºC, 4-8h
Note: The above process condition is only for reference. The actual process should be adjusted according to different types of machines,  mold design, and product design.
PC Resin, Polycarbonate Resin Plastic Raw Material
PC Resin, Polycarbonate Resin Plastic Raw MaterialPC Resin, Polycarbonate Resin Plastic Raw MaterialPC Resin, Polycarbonate Resin Plastic Raw MaterialPC Resin, Polycarbonate Resin Plastic Raw MaterialPC Resin, Polycarbonate Resin Plastic Raw MaterialPC Resin, Polycarbonate Resin Plastic Raw MaterialPC Resin, Polycarbonate Resin Plastic Raw MaterialPC Resin, Polycarbonate Resin Plastic Raw MaterialPC Resin, Polycarbonate Resin Plastic Raw Material

Are you a trading company or manufacturer?

We are a manufacturer.

 

About Sample?

5 KG Free Sample can be offered per your request.

 

About Material Color?

We can make the material to your appointed color according to Pantone/RAL#.


How does your factory control the quality?
Quality is the Priority, we always pay great importance to quality from beginning to end, we have professional QC  for item quality from spare parts to finished goods.
 

 How many days for mass production?

20 days after all artwork and 30% deposit are confirmed.
 

 How can I get the samples? is the sample free? 

7-10 days to send free samples by DHL, TNT, UPS

You Might Also Like