Steel C60e 1.0601 1.1221 Pipe or Tube for Project

China Steel C60e 1.0601 1.1221 Pipe or Tube for Project, Find details about China C60e Sheet, C60e Plate from Steel C60e 1.0601 1.1221 Pipe or Tube for Project

Basic Info.

Model NO.

C60E 1.0601 1.1221

Color

Silver

Certification

RoHS, ISO9001, ASTM, JIS, GB, En, Astmb

Technique

Cold Drawn

Surface Treatment

Mill Finish(Not Polished)

Form/Shape

Sheet, Plate, Bar, Rod, Tube, Pipe, Strip, Foil an

Payment

T/T 30% Prepayment, 70% Balance Before Delivery

Delivery Time

2-5 Working Days After Getting The Prepayment

Trademark

Taixie

Transport Package

Standard Export Packaging

Specification

0.5-200mm*500-2500mm*500-100000mm

Origin

China

HS Code

7606910000

Model NO.

C60E 1.0601 1.1221

Color

Silver

Certification

RoHS, ISO9001, ASTM, JIS, GB, En, Astmb

Technique

Cold Drawn

Surface Treatment

Mill Finish(Not Polished)

Form/Shape

Sheet, Plate, Bar, Rod, Tube, Pipe, Strip, Foil an

Payment

T/T 30% Prepayment, 70% Balance Before Delivery

Delivery Time

2-5 Working Days After Getting The Prepayment

Trademark

Taixie

Transport Package

Standard Export Packaging

Specification

0.5-200mm*500-2500mm*500-100000mm

Origin

China

HS Code

7606910000

Product Desciption

1.[ Steel C60E 1.0601 1.1221 pipe or tube]
Introduction:

Standard:

EN 10277-5: 2008 Bright steel products. Technical delivery conditions. Steels for quenching and tempering

EN 10083-2: 2006 Steels for quenching and tempering. Technical delivery conditions for non alloy steels

EN 10132-3: 2000 Cold rolled narrow steel strip for heat treatment. Technical delivery conditions. Steels for quenching and tempering

EN 10250-2: 2000 Open steel die forgings for general engineering purposes. Non-alloy quality and special steels

EN 10297-1: 2003 Seamless circular steel tubes for mechanical and general engineering purposes. Non-alloy and alloy steel tubes. Technical delivery conditions

Equivalent grades of steel C60E (1.1221)
Warning! Only for reference

EU
EN

Germany
DIN,WNr

Japan
JIS

France
AFNOR

England
BS

Italy
UNI

Spain
UNE

China
GB

Russia
GOST

Inter
ISO

C60E

Ck60

S58C

XC60

070M60

CS60

C60

C55k

60G

C60E4

Chemical composition % of steel C60E (1.1221): EN 10277-5-2008

Cr + Mo + Ni = 0.63

C	Si	Mn	Ni	P	S	Cr	Mo
0.57 - 0.65	max 0.4	0.6 - 0.9	max 0.4	max 0.03	max 0.035	max 0.4	max 0.1

Mechanical properties of steel C60E (1.1221)

Nominal thickness (mm):	to 16	16 - 100	100 - 250	250 - 500	500 - 1000
Rm - Tensile strength (MPa) (+N)	710	670	650	630	620

Nominal thickness (mm):	0.3 - 3
Rm - Tensile strength (MPa) (+A)	620

Nominal thickness (mm):	0.3 - 3
Rm - Tensile strength (MPa) (+QT)	1150-1750

Nominal thickness (mm):	5 - 10	10 - 16	16 - 40
Rm - Tensile strength (MPa) (+C)	800-1150	780-1130	730-1100

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80
Rm - Tensile strength (MPa) (+QT)	850	800	750	710

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80
ReH - Minimum yield strength (MPa) (+QT)	580	520	450	420

Nominal thickness(mm):	to 16	16 - 100	100 - 250	250 - 500	500 - 1000
Re - Upper yield strength or R_p0.2 - 0.2% proof strength (MPa) (+N)	380-390	340-350	310	275	260

Nominal thickness(mm):	0.3 - 3
R_p0.2 0.2% proof strength (MPa) (+A)	495

Nominal thickness(mm):	5 - 10	10 - 16	16 - 40
R_p0.2 0.2% proof strength (MPa) (+C)	630	550	480

Nominal thickness (mm):	0.3 - 3
A - Min. elongation Lo = 80 mm (%) (+A)	17

Nominal thickness (mm):	5 - 10	10 - 16	16 - 40
A - Min. elongation at fracture (%) (+C)	5	5	6

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80
A - Min. elongation at fracture (%) longitud., (+QT)	11	13	14	14

Nominal thickness (mm):	to 16	16 - 100	100 - 250
A - Min. elongation Lo = 5,65 √ So (%) (+N)	10	11	11

Brinell hardness (HBW): (+S)	255
Brinell hardness (HBW): (+A)	241
Brinell hardness (HBW): (+SH)	198 - 278
Vickers hardness ( HV): (+A)	195
Vickers hardness ( HV): (+CR)	305
Vickers hardness ( HV): (+QT)	345 - 530