China Quatemary Ammonium Cationic Polymer
Main Components | Cyanoguanidine Polymer | |||
Application Fields | 1. It is mainly used for color removal treatment for high-colority waste water from dyestuffs plants. 2. It is suitable to treat waste water with activated, acidic and disperse dyestuffs. 3. It can also be used to treat waste water from textile industry and dye houses, pigment industry, printing ink industry and paper industry. 4. It also can be used in the production process of paper & pulp as retention agent. | |||
Advantages: | 1.Stronger decolorization(>95%) and removal of COD,BOD(40_70) 2.Faster sedimentation, better flocculation 3.Non-pollution(no aluminum, chlorine, heavy metal ions ect.) | |||
Specifications: | Item | BWD-01 | BWD-03 | |
Appearance | colorless or light-color sticky liquid | |||
Dynamic viscosity (cps,20°C) | 50-250 M PA. S (20 degree celsius ) | |||
pH (30% water solution) | 1.0~3.0 | 3.0~5.0 | ||
Solid content % | ≥50 | ≥50 | ||
Note:We can produce according to customers' different s. | ||||
Application Method: | 1. Make solution of BWD-01, mix with 40 times water to have 2.5% solution for use. 2. Make PAC solution, 1-3% Al2O3 3. Have solution of anionic Polyelectrolyte, 0.1%. 4. Have effluent, test pH value, adjust pH value to 8-9.(It is very important, higher or lower pH, BWD-01 works not well) 5. Add PAC solution, mix with effluent completely. about 1-3 minutes 6. Add BWD-01 solution, mix with effluent completely, about 5-10 minutes 7. Add small content of anionic polyelectrolyte solution, mix slowly to have big floc. 8. Sedimentation 9. Check color for treated effluent 10. Adjust dosage of BWD-01 and PAC to do more test to have better testing result. | |||
Package & Storage: | 1. It is harmless, no-flammable and non-explosive, it can be stored at room temperature, it can not be placed in the sun. 2. It is packaged in plastic drums with each containing 30kg, 250kg, 1250kg , or others according to the requirements of clients. 3. Storage temperature: 5-30°C. 4. The product would show slightly stratification or appear white at low temperature. There is no negative impact on the performance after mixing up. |