Aluminum Ingot High Quality A7/A8/A9 Aluminum Ingot for Kitchenware, Automobile Manufacturing, Mechanical Equipment

China Aluminum Ingot High Quality A7/A8/A9 Aluminum Ingot for Kitchenware, Automobile Manufacturing, Mechanical Equipment, Find details about China Ingot, Aluminum from Aluminum Ingot High Quality A7/A8/A9 Aluminum Ingot for Kitchenware, Automobile Manufacturing, Mechanical Equipment

Basic Info.

Model NO.

ASTM

Trademark

SHENGLING

Transport Package

Export Standard Package

Specification

25Kg/Ingot, net weight 1000kg/case

Origin

China

HS Code

7601109000

Model NO.

ASTM

Trademark

SHENGLING

Transport Package

Export Standard Package

Specification

25Kg/Ingot, net weight 1000kg/case

Origin

China

HS Code

7601109000

Product Desciption

Type	Composition(%)
	AL ≥	Impurities ≤
	AL ≥	Fe	Si	Cu	Ga	Mg	Zn	Others	Total
AL99.90	99.9	0.07	0.05	0.005	0.02	0.01	0.025	0.016	0.1
AL99.85	99.85	0.12	0.08	0.005	0.03	0.02	0.03	0.015	0.15
AL99.7A	99.7	0.2	0.1	0.01	0.03	0.02	0.03	0.03	0.3
AL99.70	99.7	0.2	0.12	0.01	0.03	0.03	0.03	0.03	0.3
AL99.60	99.6	0.25	0.16	0.01	0.03	0.03	0.03	0.03	0.49
AL99.50	99.5	0.3	0.22	0.02	0.03	0.05	0.05	0.03	0.5
AL99.00	99	0.5	0.42	0.02	0.05	0.05	0.05	0.05	1

Aluminum Ingots /Aluminum ingot A7 99.7% and A8 99.8% /aluminium alloy ingot

We are exclusively engaged with our expertise in offering a wide range of Aluminum Ingot. These Ingots are manufactured using the essential quality basic material. Our Ingots are well acknowledged for their enhanced durability. Offered completely manufactured Ingots are available in miscellaneous sizes at a very competitive price. Provided Ingots are checked as per the set parameters of the industry, before final dispatch.

Products Name:Pure Aluminum Ingot99.9%

Chemical Composition: al

Weight: 20/25kg

Al (Min): 99%-99.9%

Appearance: silvery white

Aluminum ingot for remelting is produced by molten salt electrolysis method using alumina and cryolite. Products meet the national standard GB/T1196-2002. The surface of ingot is clean and smooth.