Silicon Carbide Ceramic Foam Filter Porous Ceramic Filter for Foundry

China Silicon Carbide Ceramic Foam Filter Porous Ceramic Filter for Foundry, Find details about China Sic Ceramic Foam Filter, Porous Foam Filter from Silicon Carbide Ceramic Foam Filter Porous Ceramic Filter for Foundry

Basic Info.

Model NO.

BT-CFF

Porosity %

80-90

Compressive Strength (MPa)

Trademark

BESTN

Transport Package

Carton Box

Specification

40*40*20mm~150*150*50mm

Origin

Pingxiang, Jiangxi, China

HS Code

6909110000

Model NO.

BT-CFF

Porosity %

80-90

Compressive Strength (MPa)

Trademark

BESTN

Transport Package

Carton Box

Specification

40*40*20mm~150*150*50mm

Origin

Pingxiang, Jiangxi, China

HS Code

6909110000

Product Desciption

Silicon Carbide Ceramic Foam Filter Porous Ceramic Filter for Foundry

Foam Ceramic are mainly used for filtration of aluminium and aluminium alloys in foundries and cast houses . With their excellent thermal shock resistance and corrosion resistance from molten aluminum, they can effectively eliminate inclusions, reduce trapped gas and provide laminar flow, and then the filtered metal is significantly cleaner. Cleaner metal results in higher-quality castings, less scrap, and fewer inclusion defects, all of which contribute to bottom-line profit.

SIC Ceramic Foam filters are just developed as a new type molten metal filter to decrease casting flaw in recent years. With its characteristics of light-weight, high mechanical strength, large specific surface areas, high porosity, excellent thermal shock resistance, erode resistance, high-performance,SIC Ceramic Foam filter is designed for filtering impurities from molten Iron & Alloy, nodular cast iron castings, grey iron castings and malleable castings, Bronze casting, etc
Silicon Carbide Ceramic Foam Filter Porous Ceramic Filter for Foundry

Features

Ceramic foam is a new industrial ceramic products with low bulk density (0.25 ~ 0.65) g/cm³, high porosity (60% ~ 90%), and three-dimensional reticulated structure. As ceramic foam has excellent properties such like: high temperature resistance, strong chemical corrosion resistance, and large surface area as a result of high porosity, it is widely used in molten metal filtration to remove undesirable nonmetallic inclusions in the melt.

Physical Properties for Silicon Carbide Ceramic Foam Filters:

Working Temperature	≤1540°C
Porosity	80~90%
Compression Strength (Room Temperature)	≥1.0Mpa
Volume Density	0.3-0.5g/cm3
Thermal Shock Resistance	1200°C---room temperature 3 times
Application	cast iron, cast copper, cast bronze, cast brass high temperature gas filter, chemical fillings and catalysis carrier etc.

Specification for Silicon Carbide Foam Filter

Dimension (mm)	Pouring rate (kg/s)		Filtration capacity (ton)
Dimension (mm)	Grey Iron	Ductile Iron	Grey Iron	Ductile Iron
404022	4	3	65	32
505022	6	4	100	52
755022	9	6	150	75
757522	14	9	220	100
1005022	12	8	200	100
1007522	18	12	300	150
10010022	25	16	400	200
15015022	50	36	900	450

Porous ceramics are used for:

Chemical Composition for Silicon Carbide Ceramic Foam Filters:

Al2O3	SiC	SiO2	Fe2O3
≤28.00%	≥62.00%	≤10.00%	≤0.50%

Physical &chemical properties for 3 kinds of ceramic foam filter

Type	Ceramic Ceramic Filter
Material	Alumina		Silicon carbide		Zirconia
Applied temperature	≤1200celsius degree		≤1500celsius degree		≤1700celsius degree
Color	White		Grey black		Yellow
Bulk Density	0.35~0.55g/cm3		0.45~0.65g/cm3		1~1.5g/cm3
Bore Density	10~60PPI		10~60PPI		10~60PPI
Porosity	80~90%		80~90%		80~90%
Bending Strength	0.6Mpa		0.8Mpa		0.8-1.0Mpa
Compression Strength	≥0.8Mpa		≥1.0Mpa		≥1.5Mpa
Thermal Shock Resistance	Not break after 6 times thermal shock testing
Application	Molten Aluminum and Alloy	Molten Iron and Alloy		Molten Stainless Steel, Alloy and other metal in precision molding