China Plastics Raw Material Polyamide Transparent Manufacturer, Find details about China Polyamide Transparent, High Toughened PA6 from Plastics Raw Material Polyamide Transparent Manufacturer
Density | g/cm3 | ISO 1183 | 1.14 | |
Filler content | % | ISO 1172 | ||
Mold shrinkage | % | ISO 294 | Parallel | 1.2 |
Vertical | 1.8 |
Tensile strength | MPa | ISO 527 | I type sample 50mm/min | 75 |
Elongation at break | % | ISO 527 | I type sample 50mm/min Gauge length 50mm | 20 |
Flexural strength | MPa | ISO 178 | 23ºC 10mm/min | 90 |
Flexural modulus | MPa | ISO 178 | 23ºC 10mm/min | 2800 |
Izod impact strength(notched) | KJ/m2 | ISO 180 | 23ºC | 4 |
Charpy impact strength(unnotched) | KJ/m2 | ISO 179 | 23ºC | NB |
Melting point | ºC | ISO 11357-1 | 220 | |
HDT | ºC | ISO 75 | 0.45MPA | 170 |
1.8MPA | 65 |
UL Flammability | Class | UL-94 | HB | |
GWIT | IEC60695-2-13 | - |