Squeeze Roller Pattern Layer Hardfacing Wire

China Squeeze Roller Pattern Layer Hardfacing Wire, Find details about China Welding Wire, Flux Cored Welding Wire from Squeeze Roller Pattern Layer Hardfacing Wire

Basic Info.

Port:	Tianjin, China
Payment Terms:	L/C, T/T, D/P, Western Union, Paypal, Money Gram

Product Desciption

Wear Resistant Flux Cored Welding Wires For Wear Plates

1, Advantages

Chemical Composition: High carbon high chromium
Hardness: HRC 58-65
Good Performance: no clearing slag, low welding spatter, smooth surface, high welding efficiency, stable filling rate, etc.
welding wire without any joints.
Short Delivery Time: Generally, 7 days
We have many experienced professionals to research and develop welding wires according to customers' specified chemical compositions.
We can recommend proper welding wires and provide technical solutions based on working conditions.
on-site inspection and third-party inspection are available.
As an ISO9001:2008 approved manufacture, our mission is to improve our management system and provide high quality products continuously.

2, Specification

Model	Spec. (mm)	Hardness (HRC)	Main Ingredient (%)	Application and Characteristics
HD161	2.4, 2.8, 3.2	58~65	C: 3.0~5.0 Cr: 22~27	Used in wear-resistant plate single-layer hardfacing, hardness after welding up to HRC 60
HD261		57~63	C: 3.0~5.0 Cr: 22~27	Used in wear-resistant plate double-layer hardfacing, hardness after welding up to HRC 60, good impact resistance and no easy to fall off
HD361		57~63	C: 3.0~5.0 Cr: 24~30	Used in wear-resistant plate multi-layer hardfacing, hardness after welding up to HRC 60, good impact resistance and no easy to fall off
HD181		58~65	C: 3.0~5.0 Cr: 22~27	Used in thin sheet welding, hardness up to HRC 60 after welding actual thickness less than 3.0 mm, ensures good abrasion
HD161H		58~65	C: 3.0~5.0 Cr: 25~32	Deposited metal has high chromium content after welding, good abrasion. Used in single-layer hardfacing.