Welding Flux Powder for Steel Structure Sj101

China Welding Flux Powder for Steel Structure Sj101, Find details about China Welding Flux, Submerged Arc Welding Flux from Welding Flux Powder for Steel Structure Sj101

Model NO.
LH-SJ101
Application
Submerged-arc Welding
Manufacturing Method
Sintering
Aws Specification
EL8, Em12k, Eh14
Equivalent to
Lincoln P223 Welding Flux
Applications
1.Seamless Pipe 2.Struatural Steel
Standard Package
Kraft Bag with Plastic Lining Inside
Quality System
ISO9001:2008
Size
10-60mesh
Welding Speed
120m/Hour
Performance
Slag Is Easy Remove
Trademark
PANDING
Transport Package
Kraft Bag with Plastic Lining Inside
Specification
25kg/bag, 40bags/plywood pallet
Origin
Laiwu, Shandong Pr. China
HS Code
38109000
Model NO.
LH-SJ101
Application
Submerged-arc Welding
Manufacturing Method
Sintering
Aws Specification
EL8, Em12k, Eh14
Equivalent to
Lincoln P223 Welding Flux
Applications
1.Seamless Pipe 2.Struatural Steel
Standard Package
Kraft Bag with Plastic Lining Inside
Quality System
ISO9001:2008
Size
10-60mesh
Welding Speed
120m/Hour
Performance
Slag Is Easy Remove
Trademark
PANDING
Transport Package
Kraft Bag with Plastic Lining Inside
Specification
25kg/bag, 40bags/plywood pallet
Origin
Laiwu, Shandong Pr. China
HS Code
38109000
Technical data sheet    Welding Flux  SJ101

1.Specifications: 
AWS A5.17/5.23 F6A0-EL8 F6A2-EM12 F7A2-EM12K F7A4-EH14  
EN760 SA FB 1 65 AC H5    
2.Description:
SJ101 is an agglomerated fluoride-basic type flux. It is gray and round grain,mesh 10-60. it can be operated with AC and DC. ,the welding electric current can up to 1200A.It has excellent weldability, the welding bead appearance is beautiful and the slag is easy to remove. The diffusible hydrogen content in deposited metal is less than 5ml/100g,so it has very good toughness at low temperature,therefore,crack resistance is extremely high. It is suitable for submerged arc twin-wire,tandom and multi-wire welding as well as for welding with the two-run technique.
 
It should be re-dried under 300-350ºC for 2 hours. Rust,grease and moisture on the weldment should be removed before welding.3.
3.Applications: 
It can be applied to different welding wires(such as H08MnA,H10mN2,H10MnSi,H08Mn2MoA,H08Mn2SiA etc.) It is fit for welding of low-carbon steel and low alloy steel. Such as oil storage tanks,pipeline steel,ships,bridges,pressure vessels,penstocks,boilers and H-beam structural steels.

4.Chemical Composition(%)
SiO2+TiO2Al2O3+MnOCaO+MgOCaF2SP
15-2520-3025-3525≤0.06≤0.08
 
5.Mechanical Performance of the Deposited Metal
WIREYield
Point
Rel(MPa)		Tensile
Strength
Rm(MPa)		Elongation
A
(%)		Charpy V Notch Impact Strength KV2(J)
-20ºC-40ºC
EM12≥400465-550≥22≥37 
EM12K≥400490-600≥22≥50 
EH14≥400500-650≥22≥70≥50
           

Factory profile:
LAIWU HULIN WELDING MATERIALS CO.,LTD. is top three original factory of Submerged ARC welding flux in China. 
Factory was founded in 1994, quality systerm: ISO9001-2008.
Main products: SJ101,SJ101G,SJ301,SJ50,SJ601.HJ431,HJ107,HJ260 etc.
Application: Spiral steel pipe,API pipe, Structural steel, LPC Gas Cylinder, Pressure vessel, Boiler, Bridges etc.
Yearly capacity:30000mt
OEM & buyer label is ok. Technical support can be offered.