Conductive Polyamides 66

China Conductive Polyamides 66, Find details about China Conductive PA66 Plastic, 30% Carbon Fiber Nylon 66 from Conductive Polyamides 66

Model NO.
PA66-C30
Tensile Strength
230MPa
Elongation
4%
Flexural Modulus
19.8gpa
3.2mm Izod Notched Impact Strength
17.5kj/M2
Surface Resistivity
10e3 Ohm/Sq
Trademark
XIANGU
Transport Package
20kg Bag
Specification
30% carbon fiber
Origin
China
HS Code
3908101190
Model NO.
PA66-C30
Tensile Strength
230MPa
Elongation
4%
Flexural Modulus
19.8gpa
3.2mm Izod Notched Impact Strength
17.5kj/M2
Surface Resistivity
10e3 Ohm/Sq
Trademark
XIANGU
Transport Package
20kg Bag
Specification
30% carbon fiber
Origin
China
HS Code
3908101190
Conductive Polyamides 66/Conductive PA66 granule PA66-C30 was a kind of compound material with 30% carbon fiber by extruding technique.It has excellent conductive property,good heat resistance and cold resistance,abrasive resistance,chemical stability,good mechanical strength,anti-static property.resistance to environmental stress cracking.good hardness,high tensile strength.etc.

SPECIFICATIONS:
Model:PA66-C30
Color:black
Carbon fiber content(%):30
Density(g/cm3):1.3
Shrinkage-flow(%):0.2-0.3
Tensile strength(Mpa ):230
Flexural strength(Mpa):335
Elongation(% ):2-4
Flexural modulus(Gpa):19.8
3.2mm IZOD notched impact strength(KJ/m2):17.5
Heat distortion temperature(ºC):250
Flame Rating-UL:HB
Surface resistivity(ohm/sq):10E3
Baking temperature(ºC):110ºC 2-4h
Injection or extrusion temperature(ºC):250-280ºC

STORAGE:
The conductive PA66 granule should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.

PACKAGING:
Conductive Polyamides 66

PRODUCT DETAILS:
Conductive Polyamides 66
Conductive Polyamides 66
Conductive Polyamides 66
Conductive Polyamides 66
Conductive Polyamides 66
 

You Might Also Like