Engineering Grade Modified PA66 GF35 China Supplier, Find details about China PA66 GF35, PA66 GF50 from Engineering Grade Modified PA66 GF35 China Supplier
Density | g/cm3 | ISO 1183 | 1.37 | |
Filler content | % | ISO 1172 | GF35 | |
Mold shrinkage | % | ISO 294 | Parallel | 0.2 |
Vertical | 0.6 |
Tensile strength | MPa | ISO 527 | I type sample 50mm/min | 190 |
Elongation at break | % | ISO 527 | I type sample 50mm/min Gauge length 50mm | 3 |
Flexural strength | MPa | ISO 178 | 23ºC 10mm/min | 260 |
Flexural modulus | MPa | ISO 178 | 23ºC 10mm/min | 9500 |
Izod impact strength(notched) | KJ/m2 | ISO 180 | 23ºC | 15 |
Charpy impact strength(unnotched) | KJ/m2 | ISO 179 | 23ºC | 85 |
Melting point | ºC | ISO 11357-1 | 260 | |
HDT | ºC | ISO 75 | 0.45MPA | 250 |
1.8MPA | 245 |
UL Flammability | Class | UL-94 | HB | |
GWIT | IEC60695-2-13 | - |