Products

Plastic Raw Material Polyamide 6.6 PA66 GF35 Pellets

China Plastic Raw Material Polyamide 6.6 PA66 GF35 Pellets, Find details about China Nylon-66, PA 66 Nylon from Plastic Raw Material Polyamide 6.6 PA66 GF35 Pellets

Grade
Injection/Extrusion
Samples
Free
ODM/OEM
Accept
Shape
Pelltes
Quality
Stable
Trademark
TOPO NEW
Transport Package
25kg/Bag
Specification
65*40*15cm
Origin
China
HS Code
3902100090
Grade
Injection/Extrusion
Samples
Free
ODM/OEM
Accept
Shape
Pelltes
Quality
Stable
Trademark
TOPO NEW
Transport Package
25kg/Bag
Specification
65*40*15cm
Origin
China
HS Code
3902100090
Plastic Raw Material Polyamide 6.6 PA66 GF35 Pellets
Plastic Raw Material Polyamide 6.6 PA66 GF35 Pellets
Glass fiber reinforced nylon PA66 is made of PA66 resin and filled with 10-40% glass fiber.

It is a high strength, high toughness, wear resistance, and corrosion resistance. Also, the material is dimensionally stable with high heat deflection temperature, good electrical insulation, good surface smoothness, easy molding, and other advantages.

Material is approved by RoHS compliant and can be widely used in automotive parts, electronic appliances, power tools, gears, mechanical parts, and other fields.
PA66 (F0730)
 Product Description Applications
·30%66  30% glass fiber reinforced PA66· Injection molding
·  Excellent heat stability· Good mechanical properties balance
 Properties Test Method Test ConditionUnitTypical Values
Physical properties
Specific Gravity ISO 118323ºC g/cm31.35
Ash ISO 3451800ºC,30min % 30
Mechanical properties
Tensile Strength ISO 527 50mm/min MPa 150
Elongation at BreakISO 527 50mm/min %2
Flexural Modulus ISO 1782mm/min MPa 7500
Charpy Notched Impact Strength     ISO 179-1eA23ºCkJ/m2 9
Charpy Unotched Impact Strength     ISO 179-1eU23ºCkJ/m2 70
Thermal properties
Heat deflection temperatureISO 751.80MPaC245
Melting PointDSC-C262
Other properties
Mold Shrinkage internal test method48 hours after tool % 0.3-0.6
Flammability TL1010-mm/min 35
Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. Prior to use the material, please consult with TOPO Limited.
 Processing Conditions Range 
Melt Temperature260-280ºC
Mold Temperature50-80ºC
Pre-Dry needed100ºC, 4-8h
Note: The above process condition is only for reference. The actual process should be adjusted according to different types of machines,  mold design, and product design.

Plastic Raw Material Polyamide 6.6 PA66 GF35 Pellets
Plastic Raw Material Polyamide 6.6 PA66 GF35 PelletsPlastic Raw Material Polyamide 6.6 PA66 GF35 PelletsPlastic Raw Material Polyamide 6.6 PA66 GF35 PelletsPlastic Raw Material Polyamide 6.6 PA66 GF35 PelletsPlastic Raw Material Polyamide 6.6 PA66 GF35 PelletsPlastic Raw Material Polyamide 6.6 PA66 GF35 PelletsPlastic Raw Material Polyamide 6.6 PA66 GF35 PelletsPlastic Raw Material Polyamide 6.6 PA66 GF35 PelletsPlastic Raw Material Polyamide 6.6 PA66 GF35 Pellets

Are you a trading company or manufacturer?

We are a manufacturer.

 

About Sample?

5 KG Free Sample can be offered per your request.

 

About Material Color?

We can make the material to your appointed color according to Pantone/RAL#.


How does your factory control the quality?
Quality is the Priority, we always pay great importance to quality from beginning to end, we have professional QC for item quality from spare parts to finished goods.
 

 How many days for mass production?

20 days after all artwork and 30% deposit are confirmed.
 

 How can I get the samples? is the sample free? 

7-10 days to send free samples by DHL, TNT, UPS

You Might Also Like