China AISI L6 DIN 1.2714/55nicrmov7 Skt4 Forged Hot Work Tool Steel, Find details about China DIN 1.2714, AISI L6 from AISI L6 DIN 1.2714/55nicrmov7 Skt4 Forged Hot Work Tool Steel
Country | Japan | Germany | China | USA | British |
Standard | JIS G4404 | EN ISO4957 | GB/T1299 | ASTM A681 | BS 4659 |
Grade | SKT4 | 1.2714/55NiCrMoV7 | 5CrNiMo | L6 | BH224-5 |
Standard | Grade | C | Si | Mn | P | S | Cr | Ni | Mo | V |
ASTM A681 | L6 | 0.65-0.75 | 0.1-0.5 | 0.25-0.80 | 0.03 | 0.03 | 0.6-1.2 | 1.25-2.0 | 0.50 | - |
DIN EN ISO 4957 | 1.2714 | 0.50-0.60 | 0.1-0.4 | 0.60-0.90 | 0.03 | 0.02 | 0.8-1.2 | 1.50-1.8 | 0.35-0.55 | 0.05-0.15 |
55NiCrMoV7 | ||||||||||
JIS G4404 | SKT4 | 0.50-0.60 | 0.1-0.4 | 0.60-0.90 | 0.03 | 0.02 | 0.8-1.2 | 1.50-1.8 | 0.35-0.55 | 0.05-0.15 |
Size | Round | Dia 6-1200mm |
Plate/Flat/Block | Thickness 6mm-500mm | |
Width 20mm-1000mm | ||
Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
Delivery condition | Forged; Hot rolled; Cold drawn | |
Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
Payment terms | T/T;L/C;/Money gram/ Paypal | |
Trade terms | FOB; CIF; C&F; etc.. | |
Delivery time | 30-45 days | |
Application | AISI L6 is highly recommendable for Close Die Forgings due to its characteristics of high wear-resistance, extra toughness , high hardness which is achieved with Cr-Ni-Mo-V high graded alloys. Typical applications includes Arbors, blanking dies, clutch parts, forming dies,disc saws, drift pins, brake dies, hand stamps,hubs, lead and feed screws, machine parts,punches, pawls, pinions, shear blades, spindles,spring collets, swages and etc. |