China Dillidur 500 Mn13 Ar500 High Anti Abrasion Steel Plate, Find details about China Peru Steel Plate, Dillidur 500 Plate from Dillidur 500 Mn13 Ar500 High Anti Abrasion Steel Plate
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.11-0.20 | 0.38-0.55 | 1.20-1.55 | 0.005-0.020 | 0.005-0.010 | 0.01-0.60 | 0.004-0.04 | |
Hardness | 370-430HB | |||||||
Mechanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tensile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1050 | >1250 | 12 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 40 |
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.20-0.26 | 0.75-0.95 | 1.60-1.80 | 0.015-0.020 | 0.005-0.010 | 0.01-0.60 | 0.001-0.04 | |
Hardness | 420-480HB | |||||||
Mechanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tensile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1150 | >1300 | 10 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 30 |
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.25-0.35 | 0.25-1.75 | 0.40-1.60 | 0.015-0.020 | 0.005-0.010 | 0.20-0.80 | 0.001-0.03 | |
Hardness | 470-530HB | |||||||
Mechanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tensile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1250 | >1500 | 8 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 20 |
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.30-0.37 | 0.2-0.405 | 0.40-1.60 | 0.010-0.020 | 0.005-0.010 | 0.30-0.80 | 0.002-0.60 | |
Hardness | 520-580HB | |||||||
Mechanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tensile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1300 | >1550 | 6 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 12 |
Chemical Composition | steel plate | C | Si | Mn | P | S | Cr | Ni |
Thicness | % | % | % | % | % | % | % | |
2-120mm | 0.35-0.40 | 0.20-0.80 | 0.40-1.60 | 0.010-0.020 | 0.005-0.010 | 0.25-1.00 | 0.002-0.60 | |
Hardness | 560-620HB | |||||||
Mechanical Properties | 10mm thickness steel plate typical value | Yiled Strength | Tensile Strength | Elongation | ||||
Re | Rm | A5 | ||||||
Mpa | Mpa | % | ||||||
>1450 | >1650 | 5 | ||||||
Impact Toughness | 10mm thickness steel plate typical value | Test | Impact test | |||||
Temperature | Charpy-V Longitudinal | |||||||
ºC | J | |||||||
-20 | 8 |