New Conveyor Ceramic Tiles Pulley Lagging Alumina Ceramic Mats Al2O3 Ceramic Bricks Pulp Mining Cement Coal Steel China GB ISO Manufacturer, Find details about China Weldable Al2O3 Tile, Pulley Lagging from New Conveyor Ceramic Tiles Pulley Lagging Alumina Ceramic Mats Al2O3 Ceramic Bricks Pulp Mining Cement Coal Steel China GB ISO Manufacturer
Category | HC90 | HC92 | HC95 | HCT95 | HC99 | HC-ZTA | ZrO2 |
Al2O3 | ≥90% | ≥92% | ≥95% | ≥ 95% | ≥ 99% | ≥75% | / |
ZrO2 | / | / | / | / | / | ≥21% | ≥95% |
Density | >3.50g/ cm3 | >3.60g/cm3 | >3.65g/cm3 | >3.70g/cm3 | >3.83g/cm3 | >4.10g/cm3 | >5.90g/cm3 |
HV 20 | ≥900 | ≥950 | ≥1000 | ≥1100 | ≥1200 | ≥1350 | ≥1100 |
Rock Hardness HRA | ≥80 | ≥82 | ≥85 | ≥88 | ≥90 | ≥90 | ≥88 |
Bending Strength MPa | ≥180 | ≥220 | ≥250 | ≥300 | ≥330 | ≥400 | ≥800 |
Compression strength MPa | ≥970 | ≥1050 | ≥1300 | ≥1600 | ≥1800 | ≥2000 | / |
Fracture Toughness KIc MPam 1/2 | ≥3.5 | ≥3.7 | ≥3.8 | ≥4.0 | ≥4.2 | ≥4.5 | ≥7.0 |
Wear Volume | ≤0.28 cm3 | ≤0.25cm3 | ≤0.20cm3 | ≤0.15cm3 | ≤0.10 cm3 | ≤0.05cm3 | ≤0.02cm3 |