Fluid Loss Additive for Water Base Drilling Emulsified Asphalt

China Fluid Loss Additive for Water Base Drilling Emulsified Asphalt, Find details about China Emulsified Asphalt, Waterproof Coating from Fluid Loss Additive for Water Base Drilling Emulsified Asphalt

Usage
Outdoor, Indoor
Transport Package
Pallet
Specification
20kg/ pail
Origin
China
Usage
Outdoor, Indoor
Transport Package
Pallet
Specification
20kg/ pail
Origin
China
Emulsified Asphalt (Primer)

Description
It  mainly uses asphalt as raw materials, with water as the dispersion medium, with other polymer such as SBS or APP to modified the asphalt, finally launch out this polymer modified asphalt waterproof coating. As soon as coating is curing at normal temperature, the materials can be formed on the surface a layer of elastic waterproof film, it can be work along to function as waterproof coat, and also can be compound with waterproof membrane to form compound waterproof system.

Features

1. The material is a water-based product, with non-toxic, no smell, non combustible characteristics, safe and reliable
2. The material is a single component, cold method construction, simple operation
3. High elongation and excellent flexibility

Application

1. It can be widely coated on horizontal and vertical surfaces.
2. Compound with all kinds of modified bitumen waterproofing membrane to composite strong waterproof layer.
3. As basic treatment agent for all kinds of modified bitumen waterproof membrane.

Construction Method

Substrate should be coated for several times. Stirring the coating and brushing the substrate evenly by rubber scraper. The next painting can be started after the former painting surface dry. The direction of former and latter coating should be mutually perpendicular. Several times of coating are needed to ensure penetration and adhesion of paint to the substrate. Surface drying time is about 6 hours at normal temperature.

Coverage
Usage of 1.0mm thickness dry film is 1.8-2.0kg/m2

Technical Data Sheet



Implement Standard: JC/T864-2008
No.ItemUnitStandardResult
1Appearence After stirring,No agglomeration,Uniform statePass
2Solid Content%≥6061.3
3Gelationh≤21.5
4Tensile StrengthMpa≥1.52
5Elongation at break%≥300345
6Water Impermeability 0.3Mpa,30minImpermeable
7Bending at low temperatureºC≤-20No crack




 