China 1.5V AAA Size Lithium Iron Primary Battery Fr03, Find details and Price about China Battery, Lithium Battery from 1.5V AAA Size Lithium Iron Primary Battery Fr03
No. | Items | Specification |
1 | Nominal Voltage | 1.70V ~1.86V |
2 | Impedance | ≤450mΩ |
3 | Typical Capacity(100mA) | 1100 ±50 mAh |
4 | Working Voltage | 1.30V at 350mA discharge rate |
5 | Max. Discharge Current | 1000 mA continuous |
6 | Discharge Cut-off Voltage | 0.80V |
7 | Volume | 3.8 cubic centimeters |
8 | Weight | Approx. 6.8~7.5 g |
9 | Lithium Content | Less than 0.5 gram per cell |
10 | Dimensions | Diameter: 10.0±0.5 mm |
Height: 43.9±0.6mm | ||
11 | Operating Temp. | -20 °C to 60 °C |
12 | Storage Temp. | -20 °C to 40 °C |
13 | Storage Humidity | ≤75 % |
14 | Shell Life | 5 Years |
No. | Item | Test Method | Criteria |
1 | Impact | A 15.8 mm diameter bar is vertically placed across the centre of the sample cell. A 9.1 kg mass is dropped from a height of 61cm onto the sample. | No explosion, No fire |
2 | Vibration | Freq: 10~55hz; Amp: 2mm; Three directions; total 90 min | No leakage, No explosion, no fire 0.02V total maximum OV changes |
3 | Crush | A sample cell is to be crushed between two flat surfaces. Force: 32mm diameter piston; Max pressure: 17.2MPa; Max force: 13KN; Released when the max pressure obtained. | No explosion, No fire |
No. | Item | Test Conditions | Criteria |
1 | Thermal test | Fresh batteries, store at 70 deg. C for 4hs; 20 deg. C for 2hs; -20 deg. C for 4hs; 20 deg. C for 2hs. All cycled 5 times | No leakage No explosion; No fire |
2 | Heating test | Fresh battery is heated in an oven. The rate of temperature raised: 5±2°C per minute; Max. temperature 150±2°C remaining for 10 minutes. | No explosion; No fire |
3 | Drop test | Fresh batteries; Height: 1m, 6 times; Each direction two times; Concrete floor | No leakage; No explosion; No fire |