Aluminum Clad Stainless Steel Bimetallic Plate Sheet
China Aluminum Clad Stainless Steel Bimetallic Plate Sheet, Find details about China Aluminum Clad Stainless Steel Bimetallic Plate, Aluminum Clad Stainless Steel Bimetallic Sheet from Aluminum Clad Stainless Steel Bimetallic Plate Sheet
Basic Info.
Model NO.
1050A, 1060, 1070.
Standard
Mil-J-24445A
Cladding Plate Thickness
Less Than 100mm
Base Plate Thickness
Less Than 500mm
Cladding Plate
1050A, 1060,1070
Trademark
Chalco Aluminum
Transport Package
Export Standard Wooden Case
Specification
According to Customer Requirement
Origin
Henan China
HS Code
7610900000
Model NO.
1050A, 1060, 1070.
Standard
Mil-J-24445A
Cladding Plate Thickness
Less Than 100mm
Base Plate Thickness
Less Than 500mm
Cladding Plate
1050A, 1060,1070
Trademark
Chalco Aluminum
Transport Package
Export Standard Wooden Case
Specification
According to Customer Requirement
Origin
Henan China
HS Code
7610900000
Product Desciption
Aluminum Clad Stainless Steel Bimetallic Plate Sheet
Aluminum has a small density, high strength of stainless steel, and they have good corrosion resistance in many media. They are used more as decorative materials and cooking utensils. Composite materials with their compositions have both physical and chemical properties, and are a new type of structural materials with wide applications.
The manufacturing methods of Al stainless steel composites include rolling, friction welding and explosive welding. In comparison, the latter has a unique advantage in producing a wide range of products and large-scale products, especially aluminum-stainless steel composite plates with different thickness ratios and large areas.
Aluminum Clad Stainless Steel Bimetallic Plate Sheet have the advantages of light weight and excellent thermal conductivity of aluminum, high strength and corrosion resistance of stainless steel, as well as excellent deep drawing performance and low cost, so they have been widely used, such as advanced cooking utensils, vehicle parts, medical devices, pressure vessels, integrated circuit lead frames. Missile shell and aircraft auxiliary power plant.
AlMg5-Aluminum -Stainless Steel Bimetal Clad Plate Sheet manufactured by explosive welding in cryogenic media; used in chemical machine manufacturing, atomic energy and cryogenic technology, and in vacuum-tight pipe joints for flight machinery, made of AlMg3-St37 steel with diameters of 12-150 mm.
In the aerospace industry, in order to make the materials with good low temperature performance and reduce the weight of the structure, the connection of the cryogenic container with liquid hydrogen and liquid oxygen and the outer pipeline is usually welded with different materials. When the weldability of two kinds of materials is very poor and the connection strength is required to be high, the pipe joints of different materials must be used for transition connection. The 304L stainless steel-Al-Cu-Mg alloy transition pipe joint manufactured by the explosive welding method of Henan Chalco has solved this problem.
Product Name: Aluminum Clad Stainless Steel Bimetallic Plate Sheet for cryogenic engineering / Thermal Engineering
Product characteristics: mainly used for cryogenic engineering, which not only reduces weight, but also ensures strength.
Aluminum has a small density, high strength of stainless steel, and they have good corrosion resistance in many media. They are used more as decorative materials and cooking utensils. Composite materials with their compositions have both physical and chemical properties, and are a new type of structural materials with wide applications.
The manufacturing methods of Al stainless steel composites include rolling, friction welding and explosive welding. In comparison, the latter has a unique advantage in producing a wide range of products and large-scale products, especially aluminum-stainless steel composite plates with different thickness ratios and large areas.
| Shear strength of Aluminum Clad Stainless Steel Bimetallic Plate Sheet | |||||||||
| Cladding plate | Base plate | H0/mm | Wg/(g.cm-2) | Sample/pieces | σt /MPa | ||||
| Metal | δ1 /mm | Metal | δ2 /mm | Maximum | Minimum | Average | |||
| Aluminum | 3 | Stainless steel | 4 | 4 | 1.0 | 6 | 93.4 | 68.9 | 79.4 |
| 12 | 8.5 | 8.5 | 1.7 | 8 | 75.3 | 33.0 | 51.0 | ||
| Peeling strength of Aluminum Clad Stainless Steel Bimetallic Plate Sheet | |||||||||
| Cladding plate | Base plate | H0/mm | Wg/(g.cm-2) | Sample/pieces | σt /MPa | ||||
| Metal | δ1 /mm | Metal | δ2 /mm | Maximum | Minimum | Average | |||
| Aluminum | 12 | Stainless steel | 18 | 8.5 | 1.7 | 16 | 89 | 26 | 57 |
Aluminum Clad Stainless Steel Bimetallic Plate Sheet have the advantages of light weight and excellent thermal conductivity of aluminum, high strength and corrosion resistance of stainless steel, as well as excellent deep drawing performance and low cost, so they have been widely used, such as advanced cooking utensils, vehicle parts, medical devices, pressure vessels, integrated circuit lead frames. Missile shell and aircraft auxiliary power plant.
AlMg5-Aluminum -Stainless Steel Bimetal Clad Plate Sheet manufactured by explosive welding in cryogenic media; used in chemical machine manufacturing, atomic energy and cryogenic technology, and in vacuum-tight pipe joints for flight machinery, made of AlMg3-St37 steel with diameters of 12-150 mm.
In the aerospace industry, in order to make the materials with good low temperature performance and reduce the weight of the structure, the connection of the cryogenic container with liquid hydrogen and liquid oxygen and the outer pipeline is usually welded with different materials. When the weldability of two kinds of materials is very poor and the connection strength is required to be high, the pipe joints of different materials must be used for transition connection. The 304L stainless steel-Al-Cu-Mg alloy transition pipe joint manufactured by the explosive welding method of Henan Chalco has solved this problem.
| Specs of Aluminum Clad Stainless Steel Bimetallic Plate Sheet | |
| Base plate | AISI 405,410,410S,429,430,304,309,316,321 |
| Cladding plate | 1050A, 1060,1070 |
| Standard | MIL-J-24445A |
| Cladding plate thickness | ≤100mm |
| Base plate thickness | ≤500mm |
| Length | ≤12000mm |
| Width | ≤4200mm |
Product Name: Aluminum Clad Stainless Steel Bimetallic Plate Sheet for cryogenic engineering / Thermal Engineering
Product characteristics: mainly used for cryogenic engineering, which not only reduces weight, but also ensures strength.
You Might Also Like
10OZ Cotton Polyester Spandex For Jeans
Auto Wiper Motor for Renault Master, 7701050898
Indoor Commercial Trampoline Center for Shopping Mall
Neonpro Series Black White Transparent Straight Type Sleeve ......
Reliable DDP Railway Shipping From Yiwu Shenzhen to EU DDP t......
Ont T24 Plank Support Bench Press, Chest Push Bench Fitness ......
Large Capacity Fashion Stylish Gift Women Ladies Work Shoppi......
New Factory Price High Quality Pin Type Forklift Forks for S......
Natural Birch Wood Double Pointed Sticks
Prefabricated Steel Structure House Project for Logistics Ce......
OEM ODM Customized Home Workout Equipment Resistance Band fo......
Nonwoven Fabric Best Cheap Painter Absorbent Cotton Fleece