2.0mm NiAl80/20 Cored wire For Flame Spray

DESCRAPTION:
Nickel clad aluminum exothermic coating powder, and the substrate with high strength, mainly used for spraying primer coating having oxidation resistance; but also as a work piece surface coating or repair. And ordinary carbon steel, alloy steel, stainless steel, nitriding steel, cast iron, cast steel, nickel, magnesium, zirconium, titanium, Monel, nickel-chromium alloy can achieve a good metallurgical bond micro.
 

TYPICAL DEPOSIT CHARACTERISTICS:   
? Typical Hardness     HRB 60-75      
? Bond Strength       9100 psi
? Deposit Rate        10 lbs /hr/100A
? Deposit Efficiency    70%
? Wire Coverage      0.9 oz/ft2 / m
? Surface Texture     *Variable
? Machineability      Good
 
 
 
SURFACE PREPARATION:
Surface should be clean, white metal,
with no oxides (rust), dirt, grease, or oil
on the surface to be coated. Note: It is
best not to handle surfaces after
cleaning.
Recommended method of preparation
is, to grit blast with 24 mesh aluminum
oxide, rough grind, or rough machine in
a lathe.
 

APPLICATION:           
? Bond Coat
? Dimensional Restoration
SPECIFICATION:
 
NOMINAL CHEMICAL COMPOSISTION (wt%):
Al  Ni
20  Bal

80Ni   20Al
 
RECOMMENDED SPRAY PARAMETERS:
* Parameters are typical and may vary depending on equipment used. Contact your equipment manufacture for optimum spray parameters.
STANDARD SIZES & PACKAGING:
Diameter               Packing             
1/8(3.17mm)         15kg/spool