YUFENGREC® Cordierite-Mullite Kiln Furniture -Plain Batts/Extruded Batts/Perforated Batts  manufactured by synthetic  cordierite  and lower alumina mullite ,through unique scientific  formula proportion of fines and aggregate , formed by vacuum extruding process , fired under high temperature . It has excellent thermal shock resistance, low creep rate , stable at high temperature performance . it is the best kiln furniture material operating between 1000-1300ºC,

 

Cordierite-Mullite  is a combination of Cordierite Phase ,Mullite Phase and Glass Phase , feature with excellent thermal shock  resistance ,high temperature resistance ,which is the most suitable  material making  kiln furniture especially service  under 1300 Deg C .

Cordierite-Mullite Kiln Furniture  are  widely used in the Table Ware , Sanitary ware , Electrical Porcelain Insulator , Powder Calcination , Technical Ceramic industry  .

Technical Data 

Item Unit BRAND 
YUFENG-S-BOAYUFENG-S-BOBYUFENG-S-BOC
AI2O3%353960
SiO2% 534935
MgO%7.585
Max Working Temperature ºC128012601350
Bulk Densityg/cm31.851.822.2
Apparent Porosity%283022
Coefficient of Thermal  Expansion
at 20ºC - 1000ºC		10-6 k-12.62.23.2
Specific Heat at 20ºCKj/Kg.k111
M.O.R. at  20ºCMPa141111
M.O.R. at 1250ºCMPa101010
Thermal Shock Resistance★★★★★★★★★★★★★
Max Working Temperature ºC128012601350
The data are average results of test under standard procedures and are subject to variation. Results should not be used for specification purposes or creating 
any contractual obligation.