Aluminum H9 and Aluminum Alloy H9 Sheet or Plate

China Aluminum H9 and Aluminum Alloy H9 Sheet or Plate, Find details about China A96063 Aluminum Bar, A96063aluminium Rod from Aluminum H9 and Aluminum Alloy H9 Sheet or Plate

Model NO.
A96063/AlMg0.7Si/H9
Surface Treatment
Mill Finish
Alloy
Alloy
Form
Sheet,Plate,Bar,Rod,Tube,Pipe,Strip,Foil an
Standard
ASTM B210 ASTM B221 ASTM B241 ASTM B345 ASTM B361
Application-1
Frame Work, Brackets, Interior & Exterior Architec
Temper-1
6063-O/T1/T4/T42/T5/T52/T6/T62/T66/T8/T83/T831
Density
2.7-2.8g/cm3
Melting Point
600-650
Trademark
Taixie
Transport Package
Standard Export Packaging
Specification
0.5-200mm*500-2500mm*500-100000mm
Origin
China
HS Code
7606910000
Model NO.
A96063/AlMg0.7Si/H9
Surface Treatment
Mill Finish
Alloy
Alloy
Form
Sheet,Plate,Bar,Rod,Tube,Pipe,Strip,Foil an
Standard
ASTM B210 ASTM B221 ASTM B241 ASTM B345 ASTM B361
Application-1
Frame Work, Brackets, Interior & Exterior Architec
Temper-1
6063-O/T1/T4/T42/T5/T52/T6/T62/T66/T8/T83/T831
Density
2.7-2.8g/cm3
Melting Point
600-650
Trademark
Taixie
Transport Package
Standard Export Packaging
Specification
0.5-200mm*500-2500mm*500-100000mm
Origin
China
HS Code
7606910000
[aluminium  alloy A96063/AlMg0.7Si/H9  ] 
Introduction:

Fabrication and Heat Treatment

Machinability

Aluminium / Aluminum 6063 alloy has average machinability.

Forming

Aluminium / Aluminum 6063 alloy has good hot or cold formability.

Welding

Aluminium / Aluminum 6063 alloy has good weldability.

Heat Treatment

Aluminium / Aluminum 6063 alloy is heat treated at 522°C (970°F) followed by quenching in water. This results in the production of T 4 temper. Other tempers can be produced by aging.

Forging

Aluminium / Aluminum 6063 alloy is hot forged at 260 to 510°C (500 to 950°F).

Hot Working

Aluminium / Aluminum 6063 alloy can be hot worked at temperatures ranging from 260 to 510°C (500 to 950°F)

Cold Working

Aluminium / Aluminum 6063 alloy has good cold working capacity.

Annealing

Aluminium / Aluminum 6063 alloy is annealed at 413°C (775°F) for 3 h followed by controlled cooling at 10 to 260°C (50 to 500°F) per hour, and air cooling.

Aging

Aluminium / Aluminum 6063 alloy can be aged at 177°C (350°F) for 8 h to produce T 6 and T 62 tempers. It can be aged at 183°C (360°F) to produce T5 temper.

Hardening

Aluminium / Aluminum 6063 alloy can be hardened by aging heat treatment and cold working.


[aluminium  alloy A96063/AlMg0.7Si/H9] 
Application:

frame work, brackets, interior & exterior architectural trim, etc.

6063 Aluminum Angle is also widely used for all types of fabrication projects where lightweight and corrosion resistance is a primary concern.

Aluminium / Aluminum 6063 alloy is used in architectural extrusions. It is also used in manufacturing windows, pipe railing, furniture, and stair rails.

[aluminium  alloy A96063/AlMg0.7Si/H9 ] 
Chemistry:

Chemical Composition

The following table shows the chemical composition of Aluminium / Aluminum 6063 alloy.

ElementContent (%)
Aluminum, Al98.9
Magnesium, Mg0.70
Silicon, Si0.40

Physical Properties

The physical properties of Aluminium / Aluminum 6063 alloy are tabulated below.

PropertiesMetricImperial
Density2.7 g/cm30.0975
Melting point622°C1150°F

Mechanical Properties

The mechanical properties of Aluminium / Aluminum 6063 alloy are outlined in the following table.

PropertiesMetricImperial
Tensile strength90 MPa13053 psi
Yield strength48 MPa6962 psi
Shear strength69 MPa10008 psi
Fatigue strength55 MPa7977 psi
Elastic modulus70-80 GPa10153-11603 ksi
Poisson's ratio0.330.33
Hardness2525

Thermal Properties

The thermal properties of Aluminium / Aluminum 6063 alloy are given in the following table.

PropertiesConditions
T (ºC)Treatment
Thermal expansion23.4 (10-6/ºC)20-100-
Thermal conductivity218 W/mK25-

[aluminium  alloy A96063/AlMg0.7Si/H9  ] 
Surface 

mill finish ,  not polished,
brushed
mirror 
embossed 
oxidized
cold-rolled
hot-rolled

[aluminium  alloy A96063/AlMg0.7Si/H9  ]
Specification:

Shape/Form : sheet,plate,bar,rod,tube,pipe,strip,foil and so on 

Surface : Mill Finish(Not Polished ) ,polished  ,colour-coated, sand blasting  , brushed,mirror ,embossed ,oxidized,anodic oxidation    cold-rolled,hot-rolled  


This  is our  warehouse :Aluminum H9 and Aluminum Alloy H9 Sheet or Plate


Aluminum H9 and Aluminum Alloy H9 Sheet or Plate