Hot Rolled Stainless Steel Coil (201 202)

China Hot Rolled Stainless Steel Coil (201 202), Find details about China Stainless Steel Coil(201 202), 201 Hr Stainless Steel Coil from Hot Rolled Stainless Steel Coil (201 202)

Model NO.
201 202
Model NO.
201 202
Hot Rolled Stainless Steel Coil (201 202)

Any special size can be customed, and the price can be discussed

Brand: TISCO, LISCO, ZPSS, Baoxin

Certification: ISO

Grade: 904L, 317L, 316TI, 316H, 316L, 316, 310S, 310H, 309S, 309H, 347, 347H, 321, 321H, 304H, 304L, 304, 301, 302, 303, 202, 304LN, 317LN, 310, 317, 314, 304TI, 321TI, 317J1, 316J1 and so on.

Surface: No. 1 No. 4 HL or as requested

Manufacture: Hot rolled/cold rolled

Standard: JIS, AISI, ASTM, GB, DIN, etc.

Delivery time: Within 7-20 working days since get the deposit

Quality: Prime quality

Package: Standard sea-worthy packaging(cover with PVC and wooden case), or as buyers' requirement

Weight of coil: As per Weight of coil

Payment terms: 30% as deposit by T/T, and the balance should be paid by T/T against copy of B/L or L/C.

Productive: 5000 tons per year

Applications: Stainless Steel Cold Coil applies to construction field, ships building industry, petroleum.
Composition  per  ASTM  A240 ASTM 201
*  Tempered  mechanical  properties  are  available  upon  request.
 
Carbon . 15  Max
Manganese 5.5  -  7.5
Phosphorus . 060  Max
Sulfur . 030  Max
Silicon 1.00  Max
Chromium 16.00  -  18.00
Nickel 3.50  -  5.50
Nitrogen . 25  Max
Molybdenum  
Mechanical  Properties  (Annealed,   Per  ASTM  A240)
UTS 75, 000  ksi  Min
Elongation  %  in  2" 40.00  Min
Rockwell  Hardness RB95.00  Max
applications  Kitchenware/Automotive/Appliance/Hardware/Food  processing
Magnetic  roperties 201  stainless  steel  flat  rolled  coil  is  non-magnetic  in  the  annealed  condition  but  becomes  magnetic  when  cold-worked.   In  some  cases,   201  may  be  substituted  for  other  higher  nickel  content  alloys.
Forming Type  201  stainless  steel  is  formable  to  most  shapes  but  will  work-harden  disallowing  the  most  severe  forming  operations  unless  annealed  prior  to  forming.