Aws A5.8 Rbcuzn-B Copper-Zinc Filler Metals for Brazing

China Aws A5.8 Rbcuzn-B Copper-Zinc Filler Metals for Brazing, Find details about China Aws A5.8 Rbcuzn-B, Welding Wire from Aws A5.8 Rbcuzn-B Copper-Zinc Filler Metals for Brazing

Model NO.
AWS A5.8 RBCuZn-B
Standard
GB/T
Size
1.6mm (1/16 Inch)
Spool Type
D 300
Wire Weight
15kg Each Spool
Wire Type
Solid Wire
Condition
Half Hard
Surface
Smoothly
Aws
A5.8 Rbcuzn-B
Trademark
Allotech
Transport Package
15kg Each Spool
Specification
1.6mm
Origin
China
HS Code
7408220000
Model NO.
AWS A5.8 RBCuZn-B
Standard
GB/T
Size
1.6mm (1/16 Inch)
Spool Type
D 300
Wire Weight
15kg Each Spool
Wire Type
Solid Wire
Condition
Half Hard
Surface
Smoothly
Aws
A5.8 Rbcuzn-B
Trademark
Allotech
Transport Package
15kg Each Spool
Specification
1.6mm
Origin
China
HS Code
7408220000

RBCuZn-B (low-fuming brass-nickel) braze welding rods are similar to RBCuZn-A rods but contain additions of iron and manganese which serve to increase the hardness and strength. In addition, a small amount of silicon [0.04% to 0.20%] serves to control the vaporization of the zinc, yielding the "low-fuming" property. The nickel addition [0.2% to 0.8%] assures uniform distribution of the iron in the deposit.

The filler metal is used for brazing and braze welding of steel, cast iron, copper, copper alloys, nickel, nickel alloys, and stainless steel. RBCuZn-B filler metal also is used for the surfacing of steel. It is used in torch, induction, and furnace processes. Flux and joint clearances from 0.002 in to 0.005 in [0.05 mm to 0.13 mm] are suitable.

Aws A5.8 Rbcuzn-B Copper-Zinc Filler Metals for Brazing
Product NameAWSChemical CompositionCharacteristics & Application
S201ERCuSn1 Si0.3Mn0.3 Cu Rem.Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
S211ERCuSi-ASi3 Mn1 Cu RemGood mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel
S212ERCuSn-ASn5 Cu Rem.Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
S213ERCuSn-CSn8 Cu Rem.Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
S214ERCuAl-A1Al7.5 Cu Rem.Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
S215ERCuAl-A2Al9 Cu Rem.Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
S221 Cu60 Sn1 Si0.3 Zn Rem.Melting point is about 890ºC. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
S221F Cu60 Sn1 Si 0.3 Zn Rem.S221 welding rod coated with flux.
S222RBCuZn-CCu58Sn0.9Si0.1 Fe0.8 Zn Rem.Melting point is about 880ºC. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
S222FRBCuZn-CCu58Sn0.9Si0.1 Fe0.8 Zn Rem.S222 welding rod coated with flux.
S223RBCuZn-ACu59 Sn0.6 Zn Rem.Melting point is about 900ºC. Braze welding of copper, steel and cast iron.
S224 Cu62 Si0.5 Zn Rem.Melting point is about 905ºC. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
S225RBCuZn-DCu48 Ni10 Zn Rem.Melting point is about 935ºC and high strength. Braze welding of steel, nickel and carbide alloys.
S226 Cu60 Sn0.3 Si0.2 Zn Rem.Melting point is about 900ºC. Gas welding of brass, also braze welding of copper, steel and cast iron.
S227RBCuZn-BCu58Sn0.9Ni0.5 Si0.1 Fe0.8 Zn Rem.Melting point is about 880ºC. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
S229 Cu55 Ni6 Mn4 ZnRemMelting point is about 920ºC, high strength. Braze welding of steel, nickel and hard carbide.
S231ERCuNiNi30,Fe0.6,Mn1, Ti0.3,CuRemGood corrosion resistance for sea water. Suitable for joining and overlay welding of Copper Nickel alloy.
S232 Ni10,Fe1,Mn1, Ti0.2,CuRemGood corrosion resistance for sea water. Suitable for joining and overlay welding of Copper Nickel alloy.