Excellent UV Stability ABS Material

China Excellent UV Stability ABS Material, Find details about China ABS, Material from Excellent UV Stability ABS Material

Performance2
Good Mechanical Properties Balance
Standard
ISO
Touch
ABS
Specific Gravity
1.05g/Cm2
Tensile Strength
48MPa
Flexural Modulus
2100MPa
Tensile Modulus
2200MPa
Notched Charpy Impact Strength
18kj/M2
Heat Deflection Temperature
185c
Vicat Softening Temperature
95-100
Mold Shrinkage
0.4-0.8
Flammability
<100
Trademark
Customized
Specification
Customized specification
Origin
Jiangyin City, Jiangsu Province
Performance2
Good Mechanical Properties Balance
Standard
ISO
Touch
ABS
Specific Gravity
1.05g/Cm2
Tensile Strength
48MPa
Flexural Modulus
2100MPa
Tensile Modulus
2200MPa
Notched Charpy Impact Strength
18kj/M2
Heat Deflection Temperature
185c
Vicat Softening Temperature
95-100
Mold Shrinkage
0.4-0.8
Flammability
<100
Trademark
Customized
Specification
Customized specification
Origin
Jiangyin City, Jiangsu Province
S200
Excellent UV Stability ABS Material

Properties

Test Method

Test Condition

Unit

Typical Values
 Physical properties
 Specific GravityISO 118323ºCg/cm31.05
 Mechanical properties
 Tensile StrengthISO 52750mm/minMPa48
 Tensile ModulusISO 5271mm/minMPa2200
 Flexural ModulusISO 1782mm/minMPa2100

Notched Charpy Impact Strength
ISO 179-1eA23ºCkJ/m218
 Thermal properties

Heat deflection temperature
ISO 750.45 MpaºC100
1.8 Mpa95

Vicat softening temperature
ISO 306B50ºC98
 Other properties
 Mold Shrinkageinternal test method48 hours after tool%0.4-0.8
 FlammabilityTL1010-mm/min<100
:,.,,,,,.,.,.
Note: The data above is typical value for reference, not guarantee value. The data will vary with tool design such as gate type , gate location, gate number, injection molding process and part thickness. The data will vary with different color as well. Prior to use the
material, please consult with us.