We are one leading producer of Ph 15-7 Mo forged round bars, Ph 15-7 Mo forging round bars, pH15-7Mo forged/forging round bars, UNS S15700 forging/forged round bars, AISI 632 forged/forging round bars, 1.4532 forging/forged round bars factory from china
We could produce Ph 15-7 Mo, UNS S15700, 1.4532 forging/forged round bars with diameters ranging from 10MM to 6000MM and with weights from 10KGS to 15000KGS
The melting method of Ph 15-7 Mo, UNS S15700, 1.4532 material is ESR+VIR or VIM+ESR+VAR
Our Ph 15-7 Mo, UNS S15700, 1.4532 forged/forging round bars are widely used in in chemical plants and heavy vessels, pump and valve producers, and industrial blades. Separators and centrifuges, Cement industry and sugar industry, drilling platform, drilling rig, pipelines and refineries, power generation and power plants, , generators, compressors, gear boxes. Oil & gas industry, concrete mills and mixers, processing units, crystalizer equipment and so on
Our Ph 15-7 Mo, UNS S15700, 1.4532 forged/forging round bars could be 100% Ultrasonic Inspection as per the forging parts UT Test standard of ASTM A 388 or EN10228.
We could supply Ph 15-7 Mo, UNS S15700, 1.4532 forged/forging round bars material certificate as per the standard of EN10204-3.1 or EN10204-3.2 of third party
Any inquiry of Ph 15-7 Mo, UNS S15700, 1.4532 forged/forging round bars, please feel free to contact us. We are glad to quote the best price for every clients
The chemical composition of Ph 15-7 Mo bars is as follows
Aluminum | | 0.75 - 1.5 |
Carbon | | 0.09 max |
Chromium | | 14 - 16 |
Iron | | Balance |
Manganese | | 1 max |
Molybdenum | | 2 - 3 |
Nickel | | 6.5 - 7.75 |
Phosphorus | | 0.04 max |
Silicon | | 1 max |
Sulphur | | 0.03 max |
The mechanical property of Ph15-7Mo bars is as follows
Property | Condition A | Condition TH 1050 | Condition RH 950 | Condition C | Condition CH 900 |
UTS, ksi (MPa) 0.2% YS, ksi (MPa) Elongation % in 2" Hardness, Rockwell | 130 (896) 55 (372) 35 B88 | 210 (1448) 200 (1379) 7 C44 | 240 (1655) 225 (1552) 6 C48 | 220 (1517) 190 (1310) 5 C45 | 265 (1828) 260 (1793) 2 C50 |