Glass Fiber Reinforced Composite Building Template for Concrete Construction

China Glass Fiber Reinforced Composite Building Template for Concrete Construction, Find details about China Shuttering, Plywood from Glass Fiber Reinforced Composite Building Template for Concrete Construction

Basic Info.

Model NO.

Ecolite

Trademark

Longstar

Transport Package

in Bulk or Pallet

Specification

3′*6′/4′*8′

Origin

China

HS Code

3925900000

Model NO.

Ecolite

Trademark

Longstar

Transport Package

in Bulk or Pallet

Specification

3′*6′/4′*8′

Origin

China

HS Code

3925900000

Product Desciption

Product Introduction
The glass fiber reinforced composite building formwork is a three layer sandwich structure, made of MultiTex® and glass fiber reinforced polypropylene composite. The structure is guaranteed in the aspect of material mechanics of the sheet. MultiTex® ensures the strength and impact resistance of the building formwork, thereby greatly improving the service life of the formwork and achieving 200 reusable times. The low density realizes the lightweight of the formwork system, which brings convenience and cost reduction.
The glass fiber reinforced composite building formwork is a thermoplastic composite material, which is unique in its properties makes it particularly suitable for replacing some resource consuming building formwork such as wood formwork in the field of construction.

Specification
1. Standard specification (mm): 1830*915/2440*1220
2. Standard thickness (mm): 10-20.
3. Product color: gray, white.
4. Non-standard specification can be discussed.

Product Advantage
1. Low density, High bending modulus.
2. Waterproof, moisture-proof and non hygroscopic expansion.
3. It is not easy to break and deformation at the corner.
4. Easy release.
5. It can be staples, saws, drills and wrigs as wood.
6. No moldy rot.
7. It is easy to clean and repair.
8. High reusable times.
9. Environmentally friendly recyclable
10. Low cost of single use.
The mechanical properties of Ecollte® building formwork are not comparable to that of general plastic formwork products. The higher bending modulus, the less support need to use, the less likely the formwork will be destroyed, and the economic benefits will be significant.

Technical Data

Items	Unit	Test Result
Items	Unit	Longstar composite formwork	National standard
Surface hardness	HD	≥58	≥58
Notched impact strength of simply supported beam	KJ/m2	≥100	≥25
Bending strength	MPa	≥45	≥45
Bending modulus	MPa	≥4000	≥2000
Hot deformation temperature	ºC	≥150	≥80
Dimension change rate	%	≥0.2	≥0.2
Mini.temperature of construction	ºC	-40~80	-10
Combustion performance rating	level	satisfy	≥E

Comparison

Item	Composite building formwork	Plywood	Steel formwork	Aluminum formwork
Density	0.6 g/cm3 - 0.9 g/cm3	0.8 g/cm3	7.85 g/cm3	2.8 g/cm3
Antisepsis and mildew resistance	Decay resistant and mildew free	Rot and mildew	Rust	Decay resistant and mildew free
Scratch resistance	excellent	Depends on the thickness of the film.	excellent	excellent
Impact resistance	excellent	commonly	Deformation after impact	Deformation after impact
Saw, nail, twist	Easy	Easy	can not	can not
Repairability	Easy repair	Non repairable	Repairable	Repairable
Clear	Easy to clean up	Easy to clean up	not easy to clean up.	not easy to clean up.
Expected service life	More than 200 times	3-10 times	More than 100 times	More than 300 times
construction	convenient	Soybean wood fixation is needed.	Need large scale crane hoisting.	Need large scale city hoisting
Salvage value	Normal	Extremely low	high	high
average cost	Very low	high	low	low
Performance changes after moisture absorption	unchanged	Expansion and performance degradation	No change	No change